تسجيل مستخدم جديدEffect of Co and Fe on the inverse magnetocaloric properties of Ni-Mn-Sn
142
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
At certain compositions Ni-Mn-$X$ Heusler alloys ($X$: group IIIA-VA elements) undergo martensitic transformations, and many of them exhibit inverse magnetocaloric effects. In alloys where $X$ is Sn, the isothermal entropy change is largest among the Heusler alloys, particularly in Ni$_{50}$Mn$_{37}$Sn$_{13}$ where it reaches a value of 20 Jkg$^{-1}$K$^{-1}$ for a field of 5T. We substitute Ni with Fe and Co in this alloy, each in amounts of 1 at% and 3 at% to perturb the electronic concentration and examine the resulting changes in the magnetocaloric properties. Increasing both Fe and Co concentrations causes the martensitic transition temperature to decrease, whereby the substitution by Co at both compositions or substituting 1 at% Fe leads to a decrease in the magnetocaloric effect. On the other hand, the magnetocaloric effect in the alloy with 3 at% Fe leads to an increase in the value of the entropy change to about 30 Jkg$^{-1}$K$^{-1}$ at 5T.
قيم البحث
اقرأ أيضاً
The magnetocaloric effect (MCE) in paramagnetic materials has been widely used for attaining very low temperatures by applying a magnetic field isothermally and removing it adiabatically. The effect can be exploited also for room temperature refriger
ation by using recently discovered giant MCE materials. In this letter, we report on an inverse situation in Ni-Mn-Sn alloys, whereby applying a magnetic field adiabatically, rather than removing it, causes the sample to cool. This has been known to occur in some intermetallic compounds, for which a moderate entropy increase can be induced when a field is applied, thus giving rise to an inverse magnetocaloric effect. However, the entropy change found for some ferromagnetic Ni-Mn-Sn alloys is just as large as that reported for giant MCE materials, but with opposite sign. The giant inverse MCE has its origin in a martensitic phase transformation that modifies the magnetic exchange interactions due to the change in the lattice parameters.
We report a systematic study on the magneto-structural transition in Mn-rich Fe-doped Mn-Fe-Ni-Sn(Sb/In) Heusler alloys by keeping the total valence electron concentration (e/a ratio) fixed. The martensitic transition (MT) temperature is found to shi
ft by following a proportional relationship with the e/a ratio of the magnetic elements alone. The magnetic entropy change across MT for a selected sample (Mn49FeNi40Sn9In) has been estimated from three different measurement methods (isofield magnetization (M) vs temperature (T), isothermal M vs field (H) and heat capacity (HC) vs T). We observed that though the peak value of magnetic entropy change changes with the measurement methods, the broadened shape of the magnetic entropy change vs T curves and the corresponding cooling power (~140 Jkg-1) remains invariant. The equivalent adiabatic temperature change ~ -2.6 K has been obtained from indirect measurements of temperature change. Moreover, an exchange bias field ~ 783 Oe at 5 K and a magnetoresistance of -30% are also obtained in one of these materials.
Applying a magnetic field to a ferromagnetic Ni$_{50}$Mn$_{34}$In$_{16}$ alloy in the martensitic state induces a structural phase transition to the austenitic state. This is accompanied by a strain which recovers on removing the magnetic field givin
g the system a magnetically superelastic character. A further property of this alloy is that it also shows the inverse magnetocaloric effect. The magnetic superelasticity and the inverse magnetocaloric effect in Ni-Mn-In and their association with the first order structural transition is studied by magnetization, strain, and neutron diffraction studies under magnetic field.
New double perovskites LaPbMSbO6, where M2+ = Mn2+, Co2+, and Ni2+, were synthesized as polycrystals by an aqueous synthetic route at temperatures below 1000 oC. All samples are monoclinic, space group P21/n, as obtained from Rietveld analysis of X-r
ay powder diffraction patterns. The distribution of M2+ and Sb5+ among the two octahedral sites have 3% of disorder for M2+ = Ni2+, whereas for M2+ = Mn2+ and Co2+ less disorder is found. The three samples have an antiferromagnetic transition, due to the antiferromagnetic coupling between M2+ through super-superexchange paths M2+ - O2- - Sb5+ - O2- - M2+. Transition temperatures are low: 8, 10 and 17 K for Mn2+, Co2+, and Ni2+ respectively, as a consequence of the relatively long distances between the magnetic ions M2+. Besides, for LaPbMnSbO6 a small transition at 45 K was found, with ferrimagnetic characteristics, possibly as a consequence of a small disorder between Mn2+ and Sb5+. This disorder would give additional and shorter interaction paths: superexchange Mn2+ - O2- - Mn2+.
Tailoring of individual single-atom-thick layers in nanolaminated materials offers atomic-level control over material properties. Nonetheless, multielement alloying in individual atomic layers in nanolaminates is largely unexplored. Here, we report a
series of inherently nanolaminated V2(AxSn1-x)C (A=Fe, Co, Ni and Mn, and combinations thereof, with x=1/3) synthesized by an alloy-guided reaction. The simultaneous occupancy of the four magnetic elements and Sn, the individual single-atom-thick A layers in the compound constitute high-entropy-alloy analogues, two-dimensional in the sense that the alloying exclusively occurs in the A layers. V2(AxSn1-x)C exhibit distinct ferromagnetic behavior that can be compositionally tailored from the multielement A-layer alloying. This two-dimensional alloying provides a structural-design route with expanded chemical space for discovering materials and exploit properties.