Using Lorentz transmission electron microscopy we investigate the behavior of domain walls pinned at non-topographic defects in Cr(3 nm)/Permalloy(10 nm)/Cr(5 nm) nanowires of width 500 nm. The pinning sites consist of linear defects where magnetic properties are modified by a Ga ion probe with diameter ~ 10 nm using a focused ion beam microscope. We study the detailed change of the modified region (which is on the scale of the focused ion spot) using electron energy loss spectroscopy and differential phase contrast imaging on an aberration (Cs) corrected scanning transmission electron microscope. The signal variation observed indicates that the region modified by the irradiation corresponds to ~ 40-50 nm despite the ion probe size of only 10 nm. Employing the Fresnel mode of Lorentz transmission electron microscopy, we show that it is possible to control the domain wall structure and its depinning strength not only via the irradiation dose but also the line orientation.
قيم البحث
اقرأ أيضاً
The domain wall nucleation and motion processes in Permalloy nanowires with a thickness gradient along the nanowire axis have been studied. Nanowires with widths, w = 250 nm to 3 um and a base thickness of t = 10 nm were fabricated by electron-beam l
ithography. The magnetization hysteresis loops measured on individual nanowires are compared to corresponding nanowires without a thickness gradient. The Hc vs. t/w curves of wires with and without a thickness gradient are discussed and compared to micromagnetic simulations. We find a metastability regime at values of w, where a transformation from transverse to vortex domain wall type is expected.
We present an analytical calculation of the velocity of a single 180 degree domain wall in a magnetic structure with reduced thickness and/or lateral dimension under the combined action of an external applied magnetic field and an electrical current.
As for the case of field-induced domain wall propagation in thick films, two motion regimes with different mobilities are obtained, below and far above the so-called Walker field. Additionally, for the case of current induced motion, a Walker-like current density threshold can be defined. When the dimensions of the system become comparable to the domain wall width, the threshold field and current density, stating the walls internal structure stability, are reduced by the same geometrical demagnetising factor which accounts for the confinement. This points out the fact that the velocity dependence over an extended field/current range and the knowledge of the Walker breakdown are mandatory to draw conclusions about the phenomenological Gilbert damping parameter tuning the magnetisation dynamics.
The propagation of a head-to-head magnetic domain-wall (DW) or a tail-to-tail DW in a magnetic nanowire under a static field along the wire axis is studied. Relationship between the DW velocity and DW structure is obtained from the energy considerati
on. The role of the energy dissipation in the field-driven DW motion is clarified. Namely, a field can only drive a domain-wall propagating along the field direction through the mediation of a damping. Without the damping, DW cannot propagate along the wire. Contrary to the common wisdom, DW velocity is, in general, proportional to the energy dissipation rate, and one needs to find a way to enhance the energy dissipation in order to increase the propagation speed. The theory provides also a nature explanation of the wire-width dependence of the DW velocity and velocity oscillation beyond Walker breakdown field.
Using magnetic force microscopy and micromagnetic simulations, we studied the effect of Oersted magnetic fields on the chirality of transverse magnetic domain walls in Fe$_{20}$Ni$_{80}$/Ir bilayer nanostrips. Applying nanosecond current pulses with
a current density of around $2times10^{12}$ A/m$^2$, the chirality of a transverse domain wall could be switched reversibly and reproducibly. These current densities are similar to the ones used for current-induced domain wall motion, indicating that the Oersted field may stabilize the transverse wall chirality during current pulses and prevent domain wall transformations.
We study the formation and control of metastable states of pairs of domain walls in cylindrical nanowires of small diameter where the transverse walls are the lower energy state. We show that these pairs form bound states under certain conditions, wi
th a lifetime as long as 200ns, and are stabilized by the influence of a spin polarized current. Their stability is analyzed with a model based on the magnetostatic interaction and by 3D micromagnetic simulations. The apparition of bound states could hinder the operation of devices.