تسجيل مستخدم جديدManipulating domain wall chirality by current pulses in Permalloy/Ir nanostrips
309
0
0.0
(
0
)
تأليف
Zahid Ishaque
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Using magnetic force microscopy and micromagnetic simulations, we studied the effect of Oersted magnetic fields on the chirality of transverse magnetic domain walls in Fe$_{20}$Ni$_{80}$/Ir bilayer nanostrips. Applying nanosecond current pulses with a current density of around $2times10^{12}$ A/m$^2$, the chirality of a transverse domain wall could be switched reversibly and reproducibly. These current densities are similar to the ones used for current-induced domain wall motion, indicating that the Oersted field may stabilize the transverse wall chirality during current pulses and prevent domain wall transformations.
قيم البحث
اقرأ أيضاً
Using Lorentz transmission electron microscopy we investigate the behavior of domain walls pinned at non-topographic defects in Cr(3 nm)/Permalloy(10 nm)/Cr(5 nm) nanowires of width 500 nm. The pinning sites consist of linear defects where magnetic p
roperties are modified by a Ga ion probe with diameter ~ 10 nm using a focused ion beam microscope. We study the detailed change of the modified region (which is on the scale of the focused ion spot) using electron energy loss spectroscopy and differential phase contrast imaging on an aberration (Cs) corrected scanning transmission electron microscope. The signal variation observed indicates that the region modified by the irradiation corresponds to ~ 40-50 nm despite the ion probe size of only 10 nm. Employing the Fresnel mode of Lorentz transmission electron microscopy, we show that it is possible to control the domain wall structure and its depinning strength not only via the irradiation dose but also the line orientation.
In chiral magnetic materials, numerous intriguing phenomena such as built in chiral magnetic domain walls (DWs) and skyrmions are generated by the Dzyaloshinskii Moriya interaction (DMI). The DMI also results in asymmetric DW speed under in plane mag
netic field, which provides a useful scheme to measure the DMI strengths. However, recent findings of additional asymmetries such as chiral damping have disenabled unambiguous DMI determination and the underlying mechanism of overall asymmetries becomes under debate. By extracting the DMI-induced symmetric contribution, here we experimentally investigated the nature of the additional asymmetry. The results revealed that the additional asymmetry has a truly antisymmetric nature with the typical behavior governed by the DW chirality. In addition, the antisymmetric contribution changes the DW speed more than 100 times, which cannot be solely explained by the chiral damping scenario. By calibrating such antisymmetric contributions, experimental inaccuracies can be largely removed, enabling again the DMI measurement scheme.
The domain wall nucleation and motion processes in Permalloy nanowires with a thickness gradient along the nanowire axis have been studied. Nanowires with widths, w = 250 nm to 3 um and a base thickness of t = 10 nm were fabricated by electron-beam l
ithography. The magnetization hysteresis loops measured on individual nanowires are compared to corresponding nanowires without a thickness gradient. The Hc vs. t/w curves of wires with and without a thickness gradient are discussed and compared to micromagnetic simulations. We find a metastability regime at values of w, where a transformation from transverse to vortex domain wall type is expected.
We present an analytical theory of domain wall tilt due to a transverse in-plane magnetic field in a ferromagnetic nanostrip with out-of-plane anisotropy and Dzyaloshinskii-Moriya interaction (DMI). The theory treats the domain walls as one-dimension
al objects with orientation-dependent energy, which interact with the sample edges. We show that under an applied field the domain wall remains straight, but tilts at an angle to the direction of the magnetic field that is proportional to the field strength for moderate fields and sufficiently strong DMI. Furthermore, we obtain a nonlinear dependence of the tilt angle on the applied field at weaker DMI. Our analytical results are corroborated by micromagnetic simulations.
Domain-wall magnetoresistance and low-frequency noise have been studied in epitaxial antiferromagnetically-coupled [Fe/Cr(001)]_10 multilayers and ferromagnetic Co line structures as a function of DC current intensity. In [Fe/Cr(001)]_10 multilayers
a transition from excess to suppressed domain-wall induced 1/f noise above current densities of j_c ~ 2*10^5 A/cm^2 has been observed. In ferromagnetic Co line structures the domain wall related noise remains qualitatively unchanged up to current densities exceeding 10^6A/cm^2. Theoretical estimates of the critical current density for a synthetic Fe/Cr antiferromagnet suggest that this effect may be attributed to current-induced domain-wall motion that occurs via spin transfer torques.