The spectral--kinetic characteristics of a ZnO:Ga single crystal upon excitation in the vacuum UV region have been studied. At a temperature of 8 K, the exciton luminescence line peaking at 3.356 eV has an extremely small half-width (7.2 meV) and a short decay time (360 ps). In the visible range, a wide luminescence band peaking at ~2.1 eV with a long luminescence time at 8 K and a decay time in the nanosecond range at 300 K is observed. The luminescence excitation spectra of ZnO:Ga have been measured in the range from 4 to 12.5 eV
قيم البحث
اقرأ أيضاً
The spectral characteristics of ZnO:Ga and ZnO:Ga,N ceramics prepared by uniaxial hot pressing have been investigated. At room temperature, the edge (exciton) band at 3.12 eV dominates in the luminescence spectra of ZnO:Ga, while a wide luminescence
band at 2.37 eV, which is likely to be due to zinc vacancies, is observed in the spectra of ZnO:Ga,N. Upon heating, the edge band maximum shifts to lower energies and the bandwidth increases. The extrapolated position of the edge-band maximum at zero temperature, Em(0) = 3.367 +/- 0.005 eV, is in agreement with the data for thin zinc oxide films. The luminescence excitation spectra in the range from 3 to 6.5 eV are reported and the mechanism of energy transfer to excitons and luminescence centers is considered.
Uniaxial hot pressing has been used to obtain ceramics based on zinc oxide, and their optical, x-ray-structure, luminescence, and scintillation characteristics have been studied. It is shown that, by changing the concentration of the dopant (Ga) and
the codopant (N), it is possible to change the intensities of the edge band (397.5 nm) and the intraband luminescence (510 nm) of the ZnO luminescence, as well as their ratio. Undoped ZnO ceramic has good transparency in the visible region and fairly high luminous yield: 9050 photons per MeV. Ceramic ZnO:Ga possesses intense edge luminescence with a falloff time of about 1 ns.
We generalize and systematize basic experimental data on optical and luminescence properties of ZnO single crystals, thin films, powders, ceramics, and nanocrystals. We consider and study mechanisms by which two main emission bands occur, a short-wav
elength band near the fundamental absorption edge and a broad long-wavelength band, the maximum of which usually lies in the green spectral range. We determine a relationship between the two luminescence bands and study in detail the possibility of controlling the characteristics of ZnO by varying the maximum position of the short-wavelength band. We show that the optical and luminescence characteristics of ZnO largely depend on the choice of the corresponding impurity and the parameters of the synthesis and subsequent treatment of the sample. Prospects for using zinc oxide as a scintillator material are discussed. Additionally, we consider experimental results that are of principal interest for practice.
Diamond displays a large variety of luminescence centers which define its optical properties and can be either created or modified by irradiation. The main purpose of the present work is to study the radiation hardness of several of such centers in h
omoepitaxial single crystal CVD diamond by following the evolution of photoluminescence and ionoluminescence upon 2 MeV proton irradiation. Luminescence decays were observed with values of the fluence at half of the starting luminescence (F1/2) of the order of 1014 cm-2. The 3H center displayed a non monotonic behavior, with a growing behavior and a subsequent decay with a rather high F1/2 value (in the order of few 1016 cm-2), maintaining at the highest fluences an intensity significantly higher than the blue A-band. A simple model based on a double-exponential trend was defined to fit with satisfactory accuracy the evolution of the 3H center. Several PL centers (namely: 3H, TR12, 491 nm, 494 nm) exhibited clear correlations and anti-correlations in their fluence dependences, which were considered in the attempt to acquire some insight into their possible alternative attributions.
The excitation efficiency and external luminescence quantum efficiency of trivalent Eu3+ ions doped into gallium nitride (GaN) was studied under optical and electrical excitation. For small pump fluences it was found that the excitation of Eu3+ ions
is limited by an efficient carrier trap that competes in the energy transfer from the host material. For large pump fluences the limited number of high-efficiency Eu3+ sites, and the small excitation cross-section of the majority Eu3+ site, limit the quantum efficiency. At low temperatures under optimal excitation conditions, the external luminescence quantum efficiency reached a value of 46%. These results show the high potential for this material as an efficient light emitter, and demonstrates the importance of the excitation conditions on the light output efficiency.