تسجيل مستخدم جديدDetailed transport investigation of the magnetic anisotropy of (Ga,Mn)As
252
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
This paper discusses transport methods for the investigation of the (Ga,Mn)As magnetic anisotropy. Typical magnetoresistance behaviour for different anisotropy types is discussed, focusing on an in depth discussion of the anisotropy fingerprint technique and extending it to layers with primarily uniaxial magnetic anisotropy. We find that in all (Ga,Mn)As films studied, three anisotropy components are always present. The primary biaxial along ([100] and [010]) along with both uniaxial components along the [110] and [010] crystal directions which are often reported separately. Various fingerprints of typical (Ga,Mn)As transport samples at 4 K are included to illustrate the variation of the relative strength of these anisotropy terms. We further investigate the temperature dependence of the magnetic anisotropy and the domain wall nucleation energy with the help of the fingerprint method.
قيم البحث
اقرأ أيضاً
We obtain control of magnetic anisotropy in epitaxial (Ga,Mn)As by anisotropic strain relaxation in patterned structures. The strain in the structures is characterized using sophisticated X-ray techniques. The magnetic anisotropy before patterning of
the layer, which shows biaxial easy axes along [100] and [010], is replaced by a hard axis in the direction of large elastic strain relaxation and a uniaxial easy axis in the direction where pseudomorphic conditions are retained. This strong anisotropy can not be explained by shape anisotropy and is attributed solely to lattice strain relaxation. Upon increasing the uniaxial strain anisotropy in the (Ga,Mn)As stripes, we also observe an increase in magnetic anisotropy.
We present an experimental and theoretical study of magnetocrystalline anisotropies in arrays of bars patterned lithographically into (Ga,Mn)As epilayers grown under compressive lattice strain. Structural properties of the (Ga,Mn)As microbars are inv
estigated by high-resolution X-ray diffraction measurements. The experimental data, showing strong strain relaxation effects, are in good agreement with finite element simulations. SQUID magnetization measurements are performed to study the control of magnetic anisotropy in (Ga,Mn)As by the lithographically induced strain relaxation of the microbars. Microscopic theoretical modeling of the anisotropy is performed based on the mean-field kinetic-exchange model of the ferromagnetic spin-orbit coupled band structure of (Ga,Mn)As. Based on the overall agreement between experimental data and theoretical modeling we conclude that the micropatterning induced anisotropies are of the magnetocrystalline, spin-orbit coupling origin.
The dependence of the magnetic anisotropy of As-capped (Ga,Mn)As epilayers on the annealing parameters - temperature and time - has been investigated. A uniaxial magnetic anisotropy is evidenced, whose orientation with respect to the crystallographic
axes changes upon annealing from [-110] for the as-grown samples to [110] for the annealed samples. Both cubic an uniaxial anisotropies are tightly linked to the concentration of charge carriers, the magnitude of which is controlled by the annealing process.
Atomic Force Microscopy and Grazing incidence X-ray diffraction measurements have revealed the presence of ripples aligned along the $[1bar{1}0]$ direction on the surface of (Ga,Mn)As layers grown on GaAs(001) substrates and buffer layers, with perio
dicity of about 50 nm in all samples that have been studied. These samples show the strong symmetry breaking uniaxial magnetic anisotropy normally observed in such materials. We observe a clear correlation between the amplitude of the surface ripples and the strength of the uniaxial magnetic anisotropy component suggesting that these ripples might be the source of such anisotropy.
A (Ga,Mn)As nanoelectromechanical resonator is used to obtain the first direct measurement of magnetostriction in a dilute magnetic semiconductor. Field-dependent magnetoelastic stress induces shifts in resonance frequency that can be discerned with
a high resolution electromechanical transduction scheme. By monitoring the field dependence, the magnetostriction and anisotropy field constants can be simultaneously mapped over a wide range of temperatures. These results, when compared with theoretical predictions, appear to provide insight into a unique form of magnetoelastic behavior mediated by holes.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها