An extended study of the superconducting and normal-state properties of various as-grown and post-annealed RbxFe2-ySe2 single crystals is presented. Magnetization experiments evidence that annealing of RbxFe2-ySe2 at 413 K, well below the onset of ph
ase separation Tp=489 K, neither changes the magnetic nor the superconducting properties of the crystals. In addition, annealing at 563 K, well above Tp, suppresses the superconducting transition temperature Tc and leads to an increase of the antiferromagnetic susceptibility accompanied by the creation of ferromagnetic impurity phases, which are developing with annealing time. However, annealing at T=488K=Tp increases Tc up to 33.3 K, sharpens the superconducting transition, increases the lower critical field, and strengthens the screening efficiency of the applied magnetic field. Resistivity measurements of the as-grown and optimally annealed samples reveal an increase of the upper critical field along both crystallographic directions as well as its anisotropy. Muon spin rotation and scanning transmission electron microscopy experiments suggest the coexistence of two phases below Tp: a magnetic majority phase of Rb2Fe4Se5 and a non-magnetic minority phase of Rb0.5Fe2Se2. Both microscopic techniques indicate that annealing the specimens just at Tp does not affect the volume fraction of the two phases, although the magnetic field distribution in the samples changes substantially. This suggests that the microstructure of the sample, caused by mesoscopic phase separation, is modified by annealing just at Tp, leading to an improvement of the superconducting properties of RbxFe2-ySe2 and an enhancement of Tc.
The iron arsenide RbFe_2As_2 with the ThCr_2Si_2-type structure is found to be a bulk superconductor with T_c=2.6 K. The onset of diamagnetism was used to estimate the upper critical field H_c2(T), resulting in dH_c2/dT=-1.4 T/K and an extrapolated H
_c2(0)=2.5 T. As a new representative of iron pnictide superconductors, superconducting RbFe_2As_2 contrasts with BaFe_2As_2, where the Fermi level is higher and a magnetic instability is observed. Thus, the solid solution series (Rb,Ba)Fe_2As_2 is a promising system to study the crossover from superconductivity to magnetism.
Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated for 9% Ba,
shifted by 1.1 Angstroem away from the Ba site towards the (Fe_2As_2)-layers. The upper critical field deduced from resistance measurements is anisotropic with slopes of 7.1(3) T/K (H || ab-plane) and 4.2(2) T/K (H || c-axis), sufficiently far below T_c. The extracted upper critical field anisotropy of 3 close to T_c, is in good agreement with the estimate from magnetic torque measurements. This indicates that the electronic properties in the doped BaFe_2As_2 compound are significantly more isotropic than those in the LnFeAsO family. The in-plane critical current density at 5 K exceeds 10^6 A/cm^2, making Ba_{1-x}Rb_xFe_2As_2 a promising candidate for technical applications.