We measure the temperature dependence of the Raman spectra of metallic and semiconducting nanotubes. We show that the different trend in metallic tubes is due to phonon re-normalization induced by the variation in electronic temperature, which is mod
eled including non-adiabatic contributions to account for the dynamic, time dependent nature
We report strong variations in the Raman spectra for different single-layer graphene samples obtained by micromechanical cleavage, which reveals the presence of excess charges, even in the absence of intentional doping. Doping concentrations up to ~1
0^13 cm-2 are estimated from the G peak shift and width, and the variation of both position and relative intensity of the second order 2D peak. Asymmetric G peaks indicate charge inhomogeneity on the scale of less than 1 micron.
We demonstrate electrochemical top gating of graphene by using a solid polymer electrolyte. This allows to reach much higher electron and hole doping than standard back gating. In-situ Raman measurements monitor the doping. The G peak stiffens and sh
arpens for both electron and hole doping, while the 2D peak shows a different response to holes and electrons. Its position increases for hole doping, while it softens for high electron doping. The variation of G peak position is a signature of the non-adiabatic Kohn anomaly at $Gamma$. On the other hand, for visible excitation, the variation of the 2D peak position is ruled by charge transfer. The intensity ratio of G and 2D peaks shows a strong dependence on doping, making it a sensitive parameter to monitor charges.
We investigate graphene and graphene layers on different substrates by monochromatic and white-light confocal Rayleigh scattering microscopy. The image contrast depends sensitively on the dielectric properties of the sample as well as the substrate g
eometry and can be described quantitatively using the complex refractive index of bulk graphite. For few layers (<6) the monochromatic contrast increases linearly with thickness: the samples behave as a superposition of single sheets which act as independent two dimensional electron gases. Thus, Rayleigh imaging is a general, simple and quick tool to identify graphene layers, that is readily combined with Raman scattering, which provides structural identification.