The static and dynamic magnetic properties of tetragonally distorted Mn--Ga based alloys were investigated. Static properties are determined in magnetic fields up to 6.5~T using SQUID magnetometry. For the pure Mn$_{1.6}$Ga film, the saturation magne
tisation is 0.36~MA/m and the coercivity is 0.29~T. Partial substitution of Mn by Co results in Mn$_{2.6}$Co$_{0.3}$Ga$_{1.1}$. The saturation magnetisation of those films drops to 0.2~MA/m and the coercivity is increased to 1~T. Time-resolved magneto-optical Kerr effect (TR-MOKE) is used to probe the high-frequency dynamics of Mn--Ga. The ferromagnetic resonance frequency extrapolated to zero-field is found to be 125~GHz with a Gilbert damping, $alpha$, of 0.019. The anisotropy field is determined from both SQUID and TR-MOKE to be 4.5~T, corresponding to an effective anisotropy density of 0.81~MJ/m$^3$. Given the large anisotropy field of the Mn$_{2.6}$Co$_{0.3}$Ga$_{1.1}$ film, pulsed magnetic fields up to 60~T are used to determine the field strength required to saturate the film in the plane. For this, the extraordinary Hall effect was employed as a probe of the local magnetisation. By integrating the reconstructed in--plane magnetisation curve, the effective anisotropy energy density for Mn$_{2.6}$Co$_{0.3}$Ga$_{1.1}$ is determined to be 1.23~MJ/m$^3$.
Using circularly polarised radiation and a combination of bulk-sensitive hard X-ray photoelectron spectroscopy and X-ray-absorption spectroscopy (XAS) we studied the electronic and magnetic structure of epitaxial Mn$_{1.8}$Co$_{1.2}$Ga thin films. Sp
in resolved Bloch spectral functions, density of states as well as charge and magnetisation densities were investigated by a first-principles analysis of full potential, fully relativistic Korringa--Kohn--Rostoker calculations of the electronic structure. The valence states were experimentally investigated by using linear dichroism in the angular distribution and comparing the results to spin-resolved densities of states. The linear dichroism in the valence band enabled a symmetry analysis of the contributing states. The spectra were in good agreement with the theoretical partial density of states. The element-specific, spin-resolved, unoccupied densities of states for Co and Mn were analysed by using XAS and X-ray magnetic circular dichroism (XMCD) at the $L_{3,2}$ edges. The spectra were influenced by strong correlation effects. XMCD was used to extract the site resolved magnetic moments. The experimental values of $m_{rm Mn}=0.7:mu_B$ and $m_{rm Co}=1.05:mu_B$ agree very well with the calculated magnetic moments. Magnetic circular dichroism in angle-resolved photoelectron spectroscopy at the Mn and Co $2p$ core level exhibited a pronounced magnetic dichroism and confirmed the localised character of the Mn $d$ valence states.