The influence of the deposition pressure PO2 and substrate temperature TS during the growth of Bi2FeCrO6 thin films grown by pulsed laser deposition has been investigated. It is found that the high volatility of Bi makes the deposition very difficult
and that the growth of pure Bi2FeCrO6 thin films on SrTiO3 substrates is possible only in a narrow deposition parameter window. We find that the pure Bi2FeCrO6 phase is formed within a narrow window around an oxygen pressure PO2 =1.210-2 mbar and around a substrate temperature TS=680 degC. At lower temperature or higher pressure, Bi7.38Cr0.62O12+x_also called (b*Bi2O3)and Bi2Fe4O9 /Bi2(Fe,Cr)4O9+x phases are detected, while at lower pressure or higher temperature a (Fe,Cr)3O4 phase forms. Some of these secondary phases are not well known and have not been previously studied. We previously reported Fe/Cr cation ordering as the probable origin of the tenfold improvement in magnetization at saturation of our Bi2FeCrO6 film, compared to BiFeO3. Here, we address the effect of the degree of cationic ordering on the magnetic properties of the Bi2FeCrO6 single phase. Polarization measurements at room temperature reveal that our Bi2FeCrO6 films have excellent ferroelectric properties with ferroelectric hysteresis loops exhibiting a remanent polarization as high as 55-60 miroC/cm2 along the pseudocubic (001) direction.
The properties of epitaxial Bi2FeCrO6 thin films, recently synthesized by pulsed laser deposition, have partially confirmed the theoretical predictions (i.e. a magnetic moment of 2 muB per formula unit and a polarization of ~80 microC/cm2 at 0K). The
existence of magnetic ordering at room temperature for this material is an unexpected but very promising result that needs to be further investigated. Since magnetism is assumed to arise from the exchange interaction between the Fe and Cr cations, the magnetic behaviour is strongly dependent on both their ordering and the distance between them. We present here the successful synthesis of epitaxial Bi2FexCryO6 (BFCO x/y) films grown on SrTiO3 substrates using dual crossed beam pulsed laser deposition. The crystal structure of the films has different types of (111)-oriented superstructures depending on the deposition conditions. The multiferroic character of BFCO (x/y) films is proven by the presence of both ferroelectric and magnetic hysteresis at room temperature. The oxidation state of Fe and Cr ions in the films is shown to be 3+ only and the difference in macroscopic magnetization with Fe/Cr ratio composition could only be due to ordering of the Cr3+ and Fe3+ cations therefore to the modification of the exchange interaction between them.