A first cobalt boride with the Co:B ratio below 1:1, Co5B16, was synthesized under high-pressure high-temperature conditions. It has a unique orthorhombic structure (space group Pmma, a = 19.1736(12), b = 2.9329(1), and c = 5.4886(2) {AA}, R1 (all da
ta) = 0.037). The material is hard, paramagnetic, with a weak temperature dependence of magnetic susceptibility.
We report crystal structure, electronic structure, and magnetism of manganese tetraboride, MnB4, synthesized under high-pressure high-temperature conditions. In contrast to superconducting FeB4 and metallic CrB4, which are both orthorhombic, MnB4 fea
tures a monoclinic crystal structure. Its lower symmetry originates from a Peierls distortion of the Mn chains. This distortion nearly opens the gap at the Fermi level, but despite the strong dimerization and the proximity of MnB4 to the insulating state, we find indications for a sizable paramagnetic effective moment of about 1.7 muB/f.u., ferromagnetic spin correlations and, even more surprisingly, a prominent electronic contribution to the specific heat. However, no magnetic order has been observed in standard thermodynamic measurements down to 2 K. Altogether, this renders MnB4 a structurally simple but microscopically enigmatic material; we argue that its properties may be influenced by electronic correlations.
Single crystals of novel orthorhombic (space group Pnnm) iron tetraboride FeB4 were synthesised at pressures above 8 GPa and high temperatures. Magnetic susceptibility measurements demonstrated bulk superconductivity below 2.9 K. The putative isotope
effect on the superconducting critical temperature indicates that FeB4 is likely a phonon-mediated superconductor, which is unexpected in the light of previous knowledge on Fe-based superconductors. The discovered iron tetraboride is highly incompressible and has the nanoindentation hardness of 65(5) GPa, thus, it opens a new class of highly desirable materials combining advanced mechanical properties and superconductivity.