Strong spin-orbital coupling (SOC) was found previously to lead to dramatic effects in quantum materials, such as those found in topological insulators. It was shown theoretically that local noncentrosymmetricity resulting from the rotation of RuO$_6
$ octahedral in Sr$_3$Ru$_2$O$_7$ will also give rise to an effective SOCcite{SocSr327,MicroscopicnematicSr327}. In the presence of a magnetic field applied along a specific in-plane direction, the Fermi surface was predicted to undergo a reconstruction. Here we report results of our in-plane magnetoresistivity and magnetothermopower measurements on single crystals of Sr$_3$Ru$_2$O$_7$ with an electrical or a thermal current applied along specific crystalline directions and a magnetic field rotating in the $ab$ plane (Fig. 1a), showing a minimal value for field directions predicted by the local noncentrosymmetricity theory. Furthermore, the thermopower, and therefore, the electron entropy, were found to be suppressed as the field was applied perpendicular to the thermal current, which suggests that the spin and the momentum in Sr$_3$Ru$_2$O$_7$ are locked over substantial parts of the Fermi surface, likely originating from local noncentrosymmetricity as well.
The anisotropic paramagnetism and specific heat in Nd2Ti2O7 single crystals are investigated. Angular dependence of the magnetization and Weiss temperatures show the dominant role of the crystal field effect in the magnetization. By incorporating the
results from the diluted samples, contributions to Weiss temperature from exchange interactions and crystal field interactions are isolated. The exchange interactions are found to be ferromagnetic, while the crystal field contributes a large negative part to the Weiss temperature, along all three crystallographic directions. The specific heat under magnetic field reveals a two-level Schottky ground state scheme, due to the Zeeman splitting of the ground state doublet, and the g-factors are thus determined. These observations provide solid foundations for further investigations of Nd2Ti2O7.