We investigated the depth dependence of coherence times of nitrogen-vacancy (NV) centers through precisely depth controlling by a moderately oxidative at 580{deg}C in air. By successive nanoscale etching, NV centers could be brought close to the diam
ond surface step by step, which enable us to trace the evolution of the number of NV centers remained in the chip and to study the depth dependence of coherence times of NV centers with the diamond etching. Our results showed that the coherence times of NV centers declined rapidly with the depth reduction in their last about 22 nm before they finally disappeared, revealing a critical depth for the influence of rapid fluctuating surface spin bath. By monitoring the coherence time variation with depth, we could make a shallow NV center with long coherence time for detecting external spins with high sensitivity.
We presented a high-sensitivity temperature detection using an implanted single Nitrogen-Vacancy center array in diamond. The high-order Thermal Carr-Purcell-Meiboom-Gill (TCPMG) method was performed on the implanted single nitrogen vacancy (NV) cent
er in diamond in a static magnetic field. We demonstrated that under small detunings for the two driving microwave frequencies, the oscillation frequency of the induced fluorescence of the NV center equals approximately to the average of the detunings of the two driving fields. On basis of the conclusion, the zero-field splitting D for the NV center and the corresponding temperature could be determined. The experiment showed that the coherence time for the high-order TCPMG was effectively extended, particularly up to 108 {mu}s for TCPMG-8, about 14 times of the value 7.7 {mu}s for thermal Ramsey method. This coherence time corresponded to a thermal sensitivity of 10.1 mK/Hz1/2. We also detected the temperature distribution on the surface of a diamond chip in three different circumstances by using the implanted NV center array with the TCPMG-3 method. The experiment implies the feasibility for using implanted NV centers in high-quality diamonds to detect temperatures in biology, chemistry, material science and microelectronic system with high-sensitivity and nanoscale resolution.