We have performed continuous wave and pulsed electron spin resonance measurements of implanted bismuth donors in isotopically enriched silicon-28. Donors are electrically activated via thermal annealing with minimal diffusion. Damage from bismuth ion
implantation is repaired during thermal annealing as evidenced by narrow spin resonance linewidths (B_pp=12uT and long spin coherence times T_2=0.7ms, at temperature T=8K). The results qualify ion implanted bismuth as a promising candidate for spin qubit integration in silicon.
We report on progress in ion placement into silicon devices with scanning probe alignment. The device is imaged with a scanning force microscope (SFM) and an aligned argon beam (20 keV, 36 keV) is scanned over the transistor surface. Holes in the lev
er of the SFM tip collimate the argon beam to sizes of 1.6 um and 100 nm in diameter. Ion impacts upset the channel current due to formation of positive charges in the oxide areas. The induced changes in the source-drain current are recorded in dependence of the ion beam position in respect to the FinFET. Maps of local areas responding to the ion beam are obtained.