Superconductivity (S) and ferromagnetism (F) are probed through transport and magnetization measurements in nanometer scale HoNi$_5$-NbN (F-S) bilayers and HoNi$_5$-NbN-HoNi$_5$ (F-S-F) trilayers. The choice of materials has been made on the basis of
their comparable ordering temperatures and strong magnetic anisotropy in HoNi$_5$. We observe the normal state reentrant behavior in resistance vs. temperature plots of the F-S-F structures just below the superconducting transition in the limited range of HoNi$_5$ layer thickness d$_{HN}$ (20 nm $<$ d$_{HN}$ $<$ 80 nm) when d$_{NbN}$ is fixed at $simeq$ 10 nm. The reentrance is quenched by increasing the out-of-plane (H$_{perp}$) magnetic field and transport current where as in-plane (H$_{parallel}$) field of $leq$ 1500 Oe has no effect on the reentrance. The thermally activated flux flow characteristics of the S, F-S and F-S-F layers reveal a transition from collective pinning to single vortex pinning as we place F layers on both sides of the S film. The origin of the reentrant behavior seen here in the range of 0.74 $leq$ T$_{Curie}$/T$_C$ $leq$ 0.92 is attribute to a delicate balance between the magnetic exchange energy and the condensation energy in the interfacial regions of the trilayer.
Subsequent to our recent report of SDW type transition at 190 K and antiferromagnetic order below 20 K in EuFe2As2, we have studied the effect of K-doping on the SDW transition at high temperature and AF order at low temperature. 50% K doping suppres
ses the SDW transition and in turn gives rise to high-temperature superconductivity below T_c = 32 K, as observed in the electrical resistivity, AC susceptibility as well as magnetization. A well defined anomaly in the specific heat provides additional evidence for bulk superconductivity.
We have grown single crystals of EuFe2As2 and investigated its electrical transport and thermodynamic properties. Electrical resistivity and specific heat measurements clearly establish the intrinsic nature of magnetic phase transitions at 20 K and 1
95 K. While the high temperature phase transition is associated with the itinerant moment of Fe, the low temperature phase transition is due to magnetic order of localized Eu-moments. Band structure calculations point out a very close similarity of the electronic structure with SrFe2As2. Magnetically, the Eu and Fe2As2 sublattice are nearly de-coupled.