In this paper, we report our study on gold (Au) films with different thicknesses deposited on single layer graphene (SLG) as surface enhanced Raman scattering (SERS) substrates for the characterization of rhodamine (R6G) molecules. We find that an Au
film with a thickness of ~7 nm deposited on SLG is an ideal substrate for SERS, giving the strongest Raman signals for the molecules and the weakest photoluminescence (PL) background. While Au films effectively enhance both the Raman and PL signals of molecules, SLG effectively quenches the PL signals from the Au film and molecules. The former is due to the electromagnetic mechanism involved while the latter is due to the strong resonance energy transfer from Au to SLG. Hence, the combination of Au films and SLG can be widely used in the characterization of low concentration molecules with relatively weak Raman signals.
The optical conductivities of graphene layers are strongly dependent on their stacking orders. Our first-principle calculations show that while the optical conductivities of single layer graphene (SLG) and bilayer graphene (BLG) with Bernal stacking
are almost frequency independent in the visible region, the optical conductivity of twisted bilayer graphene (TBG) is frequency dependent, giving rise to additional absorption features due to the band folding effect. Experimentally, we obtain from contrast spectra the optical conductivity profiles of BLG with different stacking geometries. Some TBG samples show additional features in their conductivity spectra in full agreement with our calculation results, while a few samples give universal conductivity values similar to that of SLG. We propose those variations of optical conductivity spectra of TBG samples originate from the difference between the commensurate and incommensurate stackings. Our results reveal that the optical conductivity measurements of graphene layers indeed provide an efficient way to select graphene films with desirable electronic and optical properties, which would great help the future application of those large scale misoriented graphene films in photonic devices.