We observed a drastic Tc suppression caused by no more than 3 at.% of Zn doped to the optimized superconductor LaFeAsO0.85 (Tc = 26 K). The electrical resistivity and magnetic susceptibility measurements suggested that it is likely due to impurity sc
atterings rather than losing the metallic nature, seeming to support the s+/- pairing model proposed for the Fe pnictide superconductor.
A wide-range doping was achieved by a high-pressure method for TbFeAsO1-x from under doped to over doped superconducting compositions throughout the optimized superconductivity (Tc of 44 K). Tc vs. lattice constant shows a dome-shaped feature, while
Tc vs. the lattice constant likely follows a unique empirical curve over the doping range. The relatively large amount of oxygen vacancies up to 0.3 per the formula unit was introduced possibly because of the smaller replacement Tb than the other Ln (rare-earth element) in the LnFeAsO1-x system.
Na-based osmium oxide pyrochlore was synthesized for the first time by an ion-exchange method. KOs2O6 was used as a host compound. Elelectron probe micro-analysis, synchrotron x-ray diffraction analysis, and thermo-gravimetric analysis confirmed its
structure not as the beta-type but as the defect-type pyrochlore. The composition was identified as Na1.4Os2O6.H2O. Electrical resistivity, heat capacity, and magnetization measurements of the polycrystalline Na1.4Os2O6.H2O clarified absence of superconductivity above 2 K, being in contrast to what were found for the beta-pyrochlore AOs2O6 (A = Cs, Rb, K). Sommerfeld coefficient of 22 mJ K-2 mol-1 of Na1.4Os2O6.H2O was smallest among those of AOs2O6. A magnetic anomaly at ~57 K and possible associated magnetoresistance (+3.7 % at 2 K in 70 kOe) were found.
The iron oxyarsenide TbFeAsO0.85 was synthesized by a high-pressure method. A high-quality polycrystalline sample was obtained and characterized by measurements of magnetic susceptibility and electrical resistivity. Bulk superconductivity with Tc of
42 K was clearly established without an F doping usually conducted to tune on superconductivity in the iron oxypnictide.