Influence of magnetism on the superconducting properties of iron-based superconductor NdFeAsO0.88F0.12

Both DC and AC magnetization measurements were performed on the NdFeAsO0.88F0.12 superconductor to investigate the influence of magnetism on the superconducting properties of this system. The crossover of the ZFC and FC magnetic susceptibility curves under 7.5KOe was observed. The imaginary component of the first harmonics of the AC magnetic susceptibility, increases with the increasing DC field below 10K and shows frequency dependency under 7.5KOe at low temperature. The paramagnetism of Nd3+ ions tilts the magnetic hysteresis loops and broadens the hysteresis width. After correction for the paramagnetism, the field and temperature dependence of intrinsic Jcm was obtained and compared with the experimentally obtained total Jcm. The origin of the abnormal behavior of magnetization was investigated and attributed to a magnetic background, which was speculated to be caused by the spin-glass state. However, this magnetic background does not affect the flux pinning properties in this sample. The related mechanism was discussed.

Comparative study of transport and magnetic Jc in the polycrystalline iron-based superconductor NdFeAsO{0.88}F{0.12}

Polycrystalline NdFeAsO0.88F0.12 superconductors prepared by high pressure (HP) and ambient pressure (AP) method were comparatively studied by magnetization and transport measurements. Upper critical field (Hc2), irreversibility field (Hirr) and the anisotropy parameter were estimated from resistance transition curves. The broadening of transition width was observed, and ascribed to both Hc2 anisotropy and superconductivity inhomogeneity of samples. Magnetic hysteresis loops (MHLs) in low fields were measured to detect the trace of weak-link behavior. The reclosed hysteresis loops in low fields manifest that there are weak-links in both samples. Magnetization critical current density Jcm were derived from MHLs. High-pressure synthesized sample shows higher Jcm. However, by means of direct transport I-V measurements, transport critical current density Jct was very low. The Jct values for two samples are comparable. Large discrepancies between Jcm and Jct also indicate that there are weak-links in both samples. The relative mechanism is discussed in detail.