Uniaxial hot pressing has been used to obtain ceramics based on zinc oxide, and their optical, x-ray-structure, luminescence, and scintillation characteristics have been studied. It is shown that, by changing the concentration of the dopant (Ga) and
the codopant (N), it is possible to change the intensities of the edge band (397.5 nm) and the intraband luminescence (510 nm) of the ZnO luminescence, as well as their ratio. Undoped ZnO ceramic has good transparency in the visible region and fairly high luminous yield: 9050 photons per MeV. Ceramic ZnO:Ga possesses intense edge luminescence with a falloff time of about 1 ns.
Ceramics ZnO:Zn of 20mm diameter and 1.6mm thickness with an optical transparency up to 0.33 in the visible region have been prepared by hot pressing technique. Scintillating and luminescent characteristics such as emission spectra, decay time, yield
, and TSL glow curve have been measured under X-ray excitation. Two emission bands peaking at 500 and 380 nm were detected, the light output was about 80% of that for standard BGO scintillator, main decay constant was 10.4 +/- 0.1 ns. The obtained data allow us to consider the ZnO:Zn ceramics as a perspective scintillator. Finally, the investigation shows that other ZnO-based fast scintillators can be fabricated in the form of optical ceramics.