The spin polarization of Pt in Pt/NiFe2O4 and Pt/Fe bilayers is studied by interface-sensitive x-ray resonant magnetic reflectivity to investigate static magnetic proximity effects. The asymmetry ratio of the reflectivity was measured at the Pt L3 ab
sorption edge using circular polarized x-rays for opposite directions of the magnetization at room temperature. The results of the 2% asymmetry ratio for Pt/Fe bilayers are independent of the Pt thickness between 1.8 and 20 nm. By comparison with ab initio calculations, the maximum magnetic moment per spin polarized Pt atom at the interface is determined to be $(0.6pm0.1),mu_{B}$ for Pt/Fe. For Pt/NiFe2O4 the asymmetry ratio drops below the sensitivity limit of $0.02,mu_{B}$ per Pt atom. Therefore, we conclude, that the longitudinal spin Seebeck effect recently observed in Pt/NiFe2O4 is not influenced by a proximity induced anomalous Nernst effect.
We investigated the magnetic anisotropy ratio of thin sputtered polycrystalline MgB2 films on MgO substrates. Using high magnetic field measurements, we estimated an anisotropy ratio of 1.35 for T=0 K with an upper critical field of 31.74 T in the pa
rallel case and 23.5 T in the perpendicular case. Direct measurements of a magnetic-field sweep at 4.2 K show a linear behavior, confirmed by a linear fit for magnetic fields perpendicular to the film plane. Furthermore, we observed a change of up to 12% of the anisotropy ratio in dependence of the film thickness.
We present results on the longitudinal spin Seebeck effect (LSSE) shown by semiconducting ferrimagnetic NiFe2O4/Pt films from room temperature down to 50K base temperature. To the best of our knowledge, this is the first observation of spin caloric e
ffect in NiFe2O4 thin films. The temperature dependence of the conductivity has been studied in parallel to obtain information about the origin of the electric potentials detected at the Pt coverage of the ferrimagnet in order to distinguish the LSSE from the anomalous Nernst effect. Furthermore, the dependence of the LSSE on temperature gradients as well as the influence of an external magnetic field direction is investigated.