We cooled ultrathin tapered fibers to cryogenic temperatures and controllably coupled them with high-Q microsphere resonators at a wavelength close to the optical transition of diamond nitrogen vacancy centers. The 310-nm-diameter tapered fibers were
stably nanopositioned close to the microspheres with a positioning stability of approximately 10 nm over a temperature range of 7-28 K. A cavity-induced phase shift was observed in this temperature range, demonstrating a discrete transition from undercoupling to overcoupling.
Highly efficient coupling of photons from nanoemitters into single-mode optical fibers is demonstrated using tapered fibers. 7.4 +/- 1.2 % of the total emitted photons from single CdSe/ZnS nanocrystals were coupled into a 300-nm-diameter tapered fibe
r. The dependence of the coupling efficiency on the taper diameter was investigated and the coupling efficiency was found to increase exponentially with decreasing diameter. This method is very promising for nanoparticle sensing and single-photon sources.