We have synthesized various samples of the $x=2/3$ phase of sodium cobaltate Na$_{x}$CoO$_{2}$ and performed X-ray powder diffractions spectra to compare the diffraction with the structure proposed previously from NMR/NQR experiments [H. Alloul emph{
et al.}, EPL textbf{85}, 47006 (2009)]. Rietveld analysis of the data are found in perfect agreement with those, and confirm the concentration x=2/3 obtained in the synthesis procedure. They even give indications on the atomic displacements of Na inside the unit cell. The detailed NQR data allow us to identify the NQR transitions and electric field gradient (EFG) parameters for 4 cobalt sites and 3 Na sites. The spin-lattice and spin-spin relaxation rates are found much smaller for the non-magnetic Co$^{3+}$ sites than for the magnetic sites on which the holes are delocalized. The atomic ordering of the Na layers is therefore at the source of this ordered distribution of cobalt charges. The method used here to resolve the Na ordering and the subsequent Co charge order can be used valuably for other concentrations of Na.
We report $^{23}$Na and $^{59}$Co nuclear magnetic (NMR) and quadrupolar resonance (NQR) studies for the $x=2/3$ phase of the lamellar oxide Na$_{x}$CoO$_{2}$, which allowed us to establish reliably the atomic order of the Na layers and their stackin
g between the CoO$_{2}$ slabs. We evidence that the Na$^{+}$ order stabilizes filled non magnetic Co$^{3+}$ ions on 25% of the cobalt sites arranged in a triangular sublattice. The transferred holes are delocalized on the 75% complementary cobalt sites which unexpectedly display a planar cobalt kagom{e} structure. These experimental results resolve a puzzling issue by precluding localized moments pictures for the magnetic properties. They establish that the quasi ferromagnetic properties result from a narrow band connecting a frustrated arrangement of atomic orbitals, and open the route to unravel through similar studies the electronic properties of the diverse ordered phases of sodium cobaltates.