We have measured the absorption of terahertz radiation in a BCS superconductor over a broad range of frequencies from 200 GHz to 1.1 THz, using a broadband antenna-lens system and a tantalum microwave resonator. From low frequencies, the response of
the resonator rises rapidly to a maximum at the gap edge of the superconductor. From there on the response drops to half the maximum response at twice the pair-breaking energy. At higher frequencies, the response rises again due to trapping of pair-breaking phonons in the superconductor. In practice this is the first measurement of the frequency dependence of the quasiparticle creation efficiency due to pair-breaking in a superconductor. The efficiency, calculated from the different non-equilibrium quasiparticle distribution functions at each frequency, is in agreement with the measurements.
Thin-film superconductors with thickness 30 to 500 nm are used as non-equilibrium quantum detectors for photons, phonons or more exotic particles. One of the most basic questions in determining their limiting sensitivity is the efficiency with which
the quanta of interest couple to the detected quasiparticles. As low temperature superconducting resonators, thin-films are attractive candidates for producing quantum-sensitive arrayable sensors and the readout uses an additional microwave probe. We have calculated the quasiparticle generation efficiency eta_s for low energy photons in a representative, clean thin-film superconductor (Al) operating well-below its superconductingtransition temperature as a function of film thickness, within the framework of the coupled kineticequations described by Chang and Scalapino.[J. J. Chang and D. J. Scalapino, J. Low Temp. Phys. 31, 1 (1978)]. We have also included the effect of a lower frequency probe. We show that phonon loss from the thin-film reduces eta_s by as much as 40% compared to earlier models that considered relatively thick films or infinite volumes. We also show that the presence of the probe and signal enhances the generation efficiency slightly. We conclude that the ultimate limiting noise equivalent power of this class of detector is determined by the thin-film geometry.