Polycrystalline Sr1-xNdxFeAsF samples were prepared at various Nd-doping levels using both a stoichiometric mixture of the starting materials and in slight excess amounts of FeAs. Susceptibility and resistivity of the samples were studied down to 4 K
revealing a probable coexistence of superconductivity and a magnetic ordering. Temperature dependence of resistivity for all the Nd-doped samples shows the presence of a transition below 15 K most likely originating from the magnetic ordering of Nd moments, while the spin-density-wave anomaly at 175 K survives up to 0.35 Nd-doping. Superconductivity only occurs above 0.40 Nd-doping with onset maximum Tc reaching as high as 52 K.
Fluoride-doped iron-based oxypnictides containing rare-earth gadolinium (GdFeAsO0.8F0.2) and co-doping with yttrium (Gd0.8Y0.2FeAsO0.8F0.2) have been prepared via conventional solid state reaction at ambient pressure. The non-yttrium substituted oxyp
nictide show superconducting transition as high as 43.9 K from temperature dependent resistance measurements with the Meissner effect observed at a lower temperature of 40.8 K from temperature dependent magnetization measurements. By replacing a small amount of gadolinium with yttrium Tc was observed to be lowered by 10 K which might be caused by a change in the electronic or magnetic structures since the crystal structure was not altered.