We have formulated a relaxation mechanism for ferrites and ferromagnetic metals whereby the coupling between the magnetic motion and lattice is based purely on continuum arguments concerning magnetostriction. This theoretical approach contrasts with
previous mechanisms based on microscopic formulations of spin-phonon interactions employing a discrete lattice. Our model explains for the first time the scaling of the intrinsic FMR linewidth with frequency, and 1/M temperature dependence and the anisotropic nature of magnetic relaxation in ordered magnetic materials, where M is the magnetization. Without introducing adjustable parameters our model is in reasonable quantitative agreement with experimental measurements of the intrinsic magnetic resonance linewidths of important class of ordered magnetic materials, insulator or metals.
Employing a new experimental technique to measure magnetoelectric response functions, we have measured the magnetoelectric effect in composite films of nano granular metallic iron in anatase titanium dioxide at temperatures below 50 K. A magnetoelect
ric resistance is defined as the ratio of a transverse voltage to bias current as a function of the magnetic field. In contrast to the anomalous Hall resistance measured above 50 K, the magnetoelectic resistance below 50 K is significantly larger and exhibits an even symmetry with respect to magnetic field reversal $Hto -H$. The measurement technique required attached electrodes in the plane of the film composite in order to measure voltage as a function of bias current and external magnetic field. To our knowledge, the composite films are unique in terms of showing magnetoelectric effects at low temperatures, $<$ 50 K, and anomalous Hall effects at high temperatures, $>$ 50 K.