Although Sr3Ru2O7 has not been reported to exhibit superconductivity so far, ac susceptibility measurements revealed multiple superconducting transitions occurring in the Sr3Ru2O7 region cut from Sr3Ru2O7-Sr2RuO4 eutectic crystals. Based on various e
xperimental results, some of us proposed the scenario in which Sr2RuO4 thin slabs with a few layers of the RuO2 plane are embedded in the Sr3Ru2O7 region as stacking faults and multiple superconducting transitions arise from the distribution of the slab thickness. To examine this scenario, we measured the resistivity along the ab plane (rho_ab) using a Sr3Ru2O7-region sample cut from the eutectic crystal, as well as along the c axis (rho_c) using the same crystal. As a result, we detected resistance drops associated with superconductivity only in rho_ab, but not in rho_c. These results support the Sr2RuO4 thin-slab scenario. In addition, we measured the resistivity of a single crystal of pure Sr3Ru2O7 with very high quality and found that pure Sr3Ru2O7 does not exhibit superconductivity down to 15 mK.
Superconducting and normal-state properties of the beta-pyrochlore oxide KOs2O6 are studied by means of thermodynamic and transport measurements. It is shown that the superconductivity is of conventional s-wave type and lies in the extremely strong-c
oupling regime. Specific heat and resistivity measurements reveal that there are characteristic low-energy phonons that give rise to unusual scattering of carriers due to strong electron-phonon interactions. The entity of the low-energy phonons is ascribed to the heavy rattling of the K ion confined in an oversized cage made of OsO6 octahedra. It is suggested that this electron-rattler coupling mediates the Cooper pairing, resulting in the extremely strong-coupling superconductivity.