Large magnetocaloric effect has been observed in Mn3O4 around its ferrimagnetic transition at TN = 42.75 K. Field-induced isothermal entropy changes (DeltaS) were derived from both magnetic and calorimetric techniques. The maximum |DeltaS| and adiaba
tic temperature change ({Delta}Tad) at TN are 11 J kg-1 K-1 and 1.9 K, respectively, for a magnetic field change of 20 kOe. Moreover, it is found that the complex magnetic phase transitions taking place below TN produce additional -but smaller- features on DeltaS(T).
Magnetic properties of a series of (La0.7Sr0.3MnO3/SrRuO3) superlattices, where the SrRuO3 layer thickness is varying, are examined. A room-temperature magnetocaloric effect is obtained owing to the finite size effect which reduces the TC of La0.7Sr0
.3MnO3 layers. While the working temperature ranges are enlarged,, -DeltaSmax values remains similar to the values in polycrystalline La0.7Sr0.3MnO3. Consequently, the relative cooling powers are significantly improved, the microscopic mechanism of which is related to the effect of the interfaces at La0.7Sr0.3MnO3/SrRuO3 and higher nanostructural disorder. This study indicates that artificial oxide superlattices/multilayers might provide an alternative pathway in searching for efficient room-temperature magnetic refrigerators for (nano)microscale systems.