The influence of La and Nd co-substitution on the structural and magnetic properties of BiFeO3 (BFO) thin films was examined. Epitaxial thin films of pure and, La and Nd co-doped BFO on the SrRuO3 buffered single crystal SrTiO3 (001) substrate were d
eposited using pulsed laser deposition. The structural change in co doped La and Nd BFO thin films which was caused by the changes of force constant in the crystal lattice induced by ionic radii mismatch was investigated. Raman spectroscopy studies manifest the structural change in doped BFO films from rhombohedral to monoclinic distorted phase which is induced by the co substitution of La and Nd. Room temperature magnetic hysteresis curves indicated that saturation magnetization is enhanced in the doped film with saturation magnetization of ~20 emu/cm3. The dielectric and magnetic properties are effectively improved in BLNFO films compared to pure BFO thin films.
Resonant Raman spectra (RRS) of O-H and O-D vibration and libration modes, their combinations and higher harmonics have been observed in LiTaO3 polycrystalline thin films. RRS peaks are superimposed on photoluminescence (PL) spectrum. Monochromatic l
ight from a xenon lamp is used as excitation source. PL spectrum shows two broad peaks, first near the band gap in UV (4.4-4.8eV) and another in the sub band gap region (< 4.0 eV). Band gap PL along with RRS peaks are reported for the first time. Photoluminescence excitation spectrum (PLE) shows a peak at 4.8 eV. Peak positions and full width at half maximum (FWHM) of RRS peaks depend upon the excitation energy. Dispersions of the fundamental and the third harmonic of the stretching mode of O-H with excitation energy are about 800 cm-1/eV and 2000 cm-1/eV respectively. This dispersion is much higher than reported in any other material.