The effects of Ir doping on the thermoelectric properties of Pt1-xIrxSb2 (x = 0, 0.01, 0.03, and 0.1) with pyrite structure were studied. Measurements of electrical resistivity rho, Seebeck coefficient S, and thermal conductivity kappa were conducted
. The results showed an abrupt change from semiconducting behavior without Ir (x = 0) to metallic behavior at x = 0.01. The sample with x = 0.01 exhibited large S and low rho, resulting in a maximum power factor (S^2/rho) of 43 muW/cmK^2 at 400 K. The peculiar pudding mold-type electronic band dispersion could explain the enhanced thermoelectric properties in the metallic state.
Low-temperature specific heat of CaRu1-xMnxO3 was measured to clarify the role of d electrons in ferromagnetic and antiferromagnetic orders observed above x=0.2. Specific heat divided by temperature C_p/T is found to roughly follow a T^2 function, an
d relatively large magnitudes of electronic specific heat coefficient gamma were obtained in wide x range. In particular, gamma is unchanged from the value at x=0 (84 mJ/K^2 mol) in the paramagnetic state for x<=0.1, but linearly reduced with increasing x above x= 0.2. These features of gamma strongly suggest that itinerant d electrons are tightly coupled with the evolution of magnetic orders in small and intermediate Mn concentrations.