The J_{eff}=1/2 insulator Sr3Ir2O7 studied by means of angle-resolved photoemission spectroscopy

The low-energy electronic structure of the J_{eff}=1/2 spin-orbit insulator Sr3Ir2O7 has been studied by means of angle-resolved photoemission spectroscopy. A comparison of the results for bilayer Sr3Ir2O7 with available literature data for the related single-layer compound Sr2IrO4 reveals qualitative similarities and similar J_{eff}=1/2 bandwidths for the two materials, but also pronounced differences in the distribution of the spectral weight. In particuar, photoemission from the J_{eff}=1/2 states appears to be suppressed. Yet, it is found that the Sr3Ir2O7 data are in overall better agreement with band-structure calculations than the data for Sr2IrO4.

Antiferromagnetic order and domains in Sr3Ir2O7 probed by x-ray resonant scattering

This article reports a detailed x-ray resonant scattering study of the bilayer iridate compound, Sr3Ir2O7, at the Ir L2 and L3 edges. Resonant scattering at the Ir L3 edge has been used to determine that Sr3Ir2O7 is a long-range ordered antiferromagnet below TN 230K with an ordering wavevector, q=(1/2,1/2,0). The energy resonance at the L3 edge was found to be a factor of ~30 times larger than that at the L2. This remarkable effect has been seen in the single layer compound Sr2IrO4 and has been linked to the observation of a Jeff=1/2 spin-orbit insulator. Our result shows that despite the modified electronic structure of the bilayer compound, caused by the larger bandwidth, the effect of strong spin-orbit coupling on the resonant magnetic scattering persists. Using the programme SARAh, we have determined that the magnetic order consists of two domains with propagation vectors k1=(1/2,1/2,0) and k2=(1/2,-1/2,0), respectively. A raster measurement of a focussed x-ray beam across the surface of the sample yielded images of domains of the order of 100 microns size, with odd and even L components, respectively. Fully relativistic, monoelectronic calculations (FDMNES), using the Greens function technique for a muffin-tin potential have been employed to calculate the relative intensities of the L2,3 edge resonances, comparing the effects of including spin-orbit coupling and the Hubbard, U, term. A large L3 to L2 edge intensity ratio (~5) was found for calculations including spin-orbit coupling. Adding the Hubbard, U, term resulted in changes to the intensity ratio <5%.