The low-temperature antiferromagnetic state of the Sm-ions in both nonsuperconducting SmFeAsO and superconducting SmFeAsO$_{0.9}$F$_{0.1}$ single crystals was studied by magnetic torque, magnetization, and magnetoresistance measurements in magnetic f
ields up to 60~T and temperatures down to 0.6~K. We uncover in both compounds a distinct rearrangement of the antiferromagnetically ordered Sm-moments near $35-40$~T. This is seen in both, static and pulsed magnetic fields, as a sharp change in the sign of the magnetic torque, which is sensitive to the magnetic anisotropy and hence to the magnetic moment in the $ab$-plane, ({it i.e.} the FeAs-layers), and as a jump in the magnetization for magnetic fields perpendicular to the conducting planes. This rearrangement of magnetic ordering in $35-40$~T is essentially temperature independent and points towards a canted or a partially polarized magnetic state in high magnetic fields. However, the observed value for the saturation moment above this rearrangement, suggests that the complete suppression of the antiferromagnetism related to the Sm-moments would require fields in excess of 60~T. Such a large field value is particularly remarkable when compared to the relatively small N{e}el temperature $T_{rm N}simeq5$~K, suggesting very anisotropic magnetic exchange couplings. At the transition, magnetoresistivity measurements show a crossover from positive to negative field-dependence, indicating that the charge carriers in the FeAs planes are sensitive to the magnetic configuration of the rare-earth elements. This is indicates a finite magnetic/electronic coupling between the SmO and the FeAs layers which are likely to mediate the exchange interactions leading to the long range antiferromagnetic order of the Sm ions.
The iron arsenide RbFe_2As_2 with the ThCr_2Si_2-type structure is found to be a bulk superconductor with T_c=2.6 K. The onset of diamagnetism was used to estimate the upper critical field H_c2(T), resulting in dH_c2/dT=-1.4 T/K and an extrapolated H
_c2(0)=2.5 T. As a new representative of iron pnictide superconductors, superconducting RbFe_2As_2 contrasts with BaFe_2As_2, where the Fermi level is higher and a magnetic instability is observed. Thus, the solid solution series (Rb,Ba)Fe_2As_2 is a promising system to study the crossover from superconductivity to magnetism.
Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated for 9% Ba,
shifted by 1.1 Angstroem away from the Ba site towards the (Fe_2As_2)-layers. The upper critical field deduced from resistance measurements is anisotropic with slopes of 7.1(3) T/K (H || ab-plane) and 4.2(2) T/K (H || c-axis), sufficiently far below T_c. The extracted upper critical field anisotropy of 3 close to T_c, is in good agreement with the estimate from magnetic torque measurements. This indicates that the electronic properties in the doped BaFe_2As_2 compound are significantly more isotropic than those in the LnFeAsO family. The in-plane critical current density at 5 K exceeds 10^6 A/cm^2, making Ba_{1-x}Rb_xFe_2As_2 a promising candidate for technical applications.