We report anisotropic dc magnetic susceptibility $chi(T)$, electrical resistivity $rho(T)$, and heat capacity $C(T)$ measurements on the single crystals of CaFe$_{2-x}$Co$_x$As$_2$ for $x$ = 0 and 0.06. Large sized single crystals were grown by the h
igh temperature solution method with Sn as the solvent. For the pure compound with $x$ = 0, a high temperature transition at 170 K is observed which is attributed to a combined spin density wave (SDW) ordering and a structural phase transition. On the other hand, for the Co-doped samples for $x$ = 0.06, the SDW transition is suppressed while superconductivity is observed at $simeq$17 K. The superconducting transition has been confirmed from the magnetization and electrical resistivity studies. The $^{57}$Fe Mossbauer spectrum in CaFe$_2$As$_2$ indicates that the SDW ordering is incommensurate. In the Co-doped sample, a prominent paramagnetic line at 4.2 K is observed indicating a weakening of the SDW state.
We report the single crystal growth and anisotropic magnetic properties of the tetragonal RAg$_2$Ge$_2$ (R = Pr, Nd and Sm) compounds which crystallize in the ThCr$_2$Si$_2$ type crystal structure with the space group textit{I4/mmm}. The single cryst
als of RAg$_2$Ge$_2$ (R = Pr, Nd and Sm) were grown by self-flux method using Ag:Ge binary alloy as flux. From the magnetic studies on single crystalline samples we have found that PrAg$_2$Ge$_2$ and NdAg$_2$Ge$_2$ order antiferromagnetically at 12 K and 2 K respectively, thus corroborating the earlier polycrystalline results. SmAg$_2$Ge$_2$ also orders antiferromagnetically at 9.2 K. The magnetic susceptibility and magnetization show a large anisotropy and the easy axis of magnetization for PrAg$_2$Ge$_2$ and NdAg$_2$Ge$_2$ is along the [100] direction where as it changes to [001] direction for SmAg$_2$Ge$_2$. Two metamagnetic transitions were observed in NdAg$_2$Ge$_2$ at $H_{rm m1}$ = 1.25 T and $H_{rm m2}$ =3.56 T for the field parallel to [100] direction where as the magnetization along [001] direction was linear indicating the hard axis of magnetization.