A reasonable cause of absence of hump structure in thermal conductivity of MgB2 below the superconducting transition temperature (Tc) lies in the appearance of multigap structure. The gaps of lower magnitude can be suppressed by defects so that this
system becomes effectively a single gap superconductor. When such a situation is created, it is hoped that thermal conductivity will show hump below Tc. Proceeding along these lines, a sample of MgB2 with a relatively higher residual resistivity (33.3 mili-Ohm-cm)has been found to show a hump structure below Tc. The actual electronic thermal conductivity kel of this sample is less than that expected from the Wiedeman- Franz law by more than a factor of 2.6 in the considered temperature range. Modifying the Wiedeman- Franz law for the electronic contribution by replacing the Lorenz number by an effective Lorenz number Leff (L0) we have obtained two sets of kel, namely those with Leff = 0.1L0 and 0.2L0. Corresponding to these two sets of kel, two sets of the phonon thermal conductivity kph are obtained. kph has been analyzed in terms of an extended Bardeen- Rickayzen- Tewordt theory. The main result of this analysis is that the hump structure corresponds to a gap ratio of 3.5, and that large electron-point defect scattering is the main source of drastic reduction of the electronic thermal conductivity from that given by the usual Wiedeman- Franz law.
Thermoelectric power, S(T) of the Mg1-xAlxB2 system has been measured for x = 0.0, 0.1, 0.2, 0.4, 0.6, 0.8 and 1.0. XRD, resistivity and magnetization measurements are also presented. It has been found that the thermoelectric power is positive for x
= 0.4 and is negative for x = 0.6 over the entire temperature range studied up to 300 K. The thermoelectric power of x = 0.4 samples vanishes discontinuously below a certain temperature, implying existence of superconductivity. In general, the magnitude of the thermoelectric power increases with temperature up to a certain temperature, and then it starts to decrease towards zero base line. In order to explain the observed behavior of the thermoelectric power, we have used a model in which both diffusion and phonon drag processes are combined by using a phenomenological interpolation between the low and high temperature behaviors of the thermoelectric power. The considered model provides an excellent fit to the observed data. It is further found that Al doping enhances the Debye temperature.