We report the existence of ferromagnetic correlations (FMC) in paramagnetic (PM) matrix of cubic La1-xSrxMnO3-{delta} (x = 0.80, 0.85) well above its coupled structural, magnetic and electronic phase transitions. The dc-magnetization vs temperature [
M(T)] behaviour under different magnetic fields (from 100 Oe to 70 kOe) shows the presence of short range magnetic correlations up to (TFMC ~) 365 K, far above the antiferromagnetic ordering temperatures (TN =) 260 K and 238 K for x=0.80 and 0.85, respectively. More importantly the observed short-range FMC survive even up to 70 kOe, which indicates their robust nature. The temperature region between TN to TFMC is dominated by the presence of correlated ferromagnetic (FM) entities within the PM matrix and stabilized due to A-site chemical disorder. Our results further illustrate that for the studied compositions, the oxygen off-stoichiometry does not have any significant effect on the nature and strength of these FM entities; however, FM interactions increase in the oxygen deficient samples. These compositions are the unique examples, where the presence of FMC is observed in an undistorted basic cubic perovskite lattice well above TN and therefore are novel to understand the physics behind the colossal magneto-resistance effect.
Resonance Raman (RR) peaks of and stretching modes and their higher harmonics have been observed superimposed on photoluminescence (PL) spectrum of thin films. Commercial fluorine doped thin films deposited by sputtering on glass and thin films depos
ited on Si by laser ablation have been studied. The dispersions of CO and OH stretching RR modes are ~ 600 cm-1/eV and 800 cm-1 respectively. The dispersion of the third harmonic of CO stretching mode is ~ 2000 cm-1/eV. Similar dispersion of RR peak of stretching modes and higher harmonics superimposed on PL spectra has been observed in Mo1-xFexO2 thin films and SiO2 bulk glass. Large dispersion of RR peaks seems to be a common property of oxides with impurities of and .