Single crystalline CaFe2As2 and (Ca1-xNax)Fe2As2 polycrystals (0 < x < 0.66) are synthesized and characterized using structural, magnetic, electronic transport, and heat capacity measurements. These measurements show that the structural/magnetic phas
e transition in CaFe2As2 at 165 K is monotonically suppressed by the Na doping and that superconductivity can be realized over a wide doping region. For 0.3 < x < 0.36, the magnetic susceptibilities indicate the possible coexistence of the spin density wave (SDW) and superconductivity. Superconducting phases corresponding to the Na doping level in (Ca1-xNax)Fe2As2 for nominal x = 0.36, 0.4, 0.5, 0.6, and 0.66, with Tc = 17 K, 19 K, 22 K, 33 K, and 33 K, respectively, are identified. The effects of the magnetic field on the superconductivity transitions for x = 0.66 samples with high upper critical fields Hc2 approx 103 T are studied, and a phase diagram of the SDW and superconductivity as a function of the doping level is thus presented.
The effect of pressure on superconductivity of 111 type NaxFeAs is investigated through temperature dependent electrical resistance measurement in a diamond anvil cell. The superconducting transition temperature (Tc) increases from 26 K to a maximum
31 K as the pressure increases from ambient to 3 GPa. Further increasing pressure suppresses Tc drastically. The behavior of pressure tuned Tc in NaxFeAs is much different from that in LixFeAs, although they have the same Cu2Sb type structure