An experimental setup for determining the electrical resistivity of several types of thermoelectric materials over the temperature range 20 < T < 550 C is described in detail. One resistivity measurement during temperature cycling is also explained f
or Cu0.01Bi2Te2.7Se0.3 while a second measurement is made on Yb0.35Co4Sb12 as a function of time at 400 C. Both measurements confirm that the materials are thermally stable for the temperature range and time period measured. Measurements made during temperature cycling show an irreversible decrease in the electrical resistivity of Cu0.01Bi2Te2.7Se0.3 when the measuring temperature exceeds the pressing temperature. Several other possible uses of such a system include but are not limited to studying the effects of annealing and/or oxidation as a function of both temperature and time.
We have combined temperature dependent local structural measurements with first principles density functional calculations to develop a three dimensional local structure model of the misfit system [Ca2CoO3][CoO2]1.61 (referred to as Ca3Co4O9) which h
as a rock salt structure stacked incommensurately on a hexagonal CoO2 lattice. The local structural measurements reveal a low coordination of Co(2)-O bonds in the rock salt layer with large static structural disorder. The temperature dependence of the Co(1)-Co(1) bond correlations in the CoO2 layer are found to be normal above ~75K and with a very small static disorder component. An anomalous enhancement in the Co(1)-Co(1) correlations occurs at the onset of long-range magnetic order. Density functional computations suggest that the reduction of the coordination of Co(2) is due to the formation of chains of Co(2)Ox in the a-b plane linked to the Ca-O layers by c-axis Co(2)-O bonds. The reduced dimensionality introduced by the chain-like structure in the rock salt layer and high atomic order in the C