The phonon density of states (DOS) and magnetic excitation spectrum of polycrystalline BiFeO$_3$ were measured for temperatures $200 leq T leq 750,$K, using inelastic neutron scattering (INS). Our results indicate that the magnetic spectrum of BiFeO$
_3$ closely resembles that of similar Fe perovskites, such as LaFeO$_3$, despite the cycloid modulation in BiFeO$_3$. We do not find any evidence for a spin gap. A strong $T$-dependence of the phonon DOS was found, with a marked broadening of the whole spectrum, providing evidence of strong anharmonicity. This anharmonicity is corroborated by large-amplitude motions of Bi and O ions observed with neutron diffraction. These results highlight the importance of spin-phonon coupling in this material.
The effects of various transition metal dopants on the electrical and thermal transport properties of Fe1-xMxSi alloys (M= Co, Ir, Os) are reported. The maximum thermoelectric figure of merit ZTmax is improved from 0.007 at 60 K for pure FeSi to ZT =
0.08 at 100 K for 4% Ir doping. A comparison of the thermal conductivity data among Os, Ir and Co doped alloys indicates strong electron-phonon coupling in this compound. Because of this interaction, the common approximation of dividing the total thermal conductivity into independent electronic and lattice components ({kappa}Total = {kappa}electronic + {kappa}lattice) fails for these alloys. The effects of grain size on thermoelectric properties of Fe0.96Ir0.04Si alloys are also reported. The thermal conductivity can be lowered by about 50% with little or no effect on the electrical resistivity or Seebeck coefficient. This results in ZTmax = 0.125 at 100 K, still about a factor of five too low for solid-state refrigeration applications.