Cobalt nitride (Co-N) thin films prepared using a reactive magnetron sputtering process by varying the relative nitrogen gas flow (pn) are studied in this work. As pn~increases, Co(N), tcn, Co$_3$N and CoN phases are formed. An incremental increase i
n pn, after emergence of tcn~phase at pn=10p, results in a continuous expansion in the lattice constant ($a$) of tcn. For pn=30p, $a$ maximizes and becomes comparable to its theoretical value. An expansion in $a$ of tcn, results in an enhancement of magnetic moment, to the extent that it becomes even larger than pure Co. Though such higher (than pure metal) magnetic moment for Fe$_4$N thin films have been theoretically predicted and evidenced experimentally, higher (than pure Co) magnetic moment are evidenced in this work and explained in terms of large-volume high-moment model for tetra metal nitrides.
In the present work, we systematically studied the effect of Al doping on the phase formation of iron nitride (Fe-N) thin films. Fe-N thin films with different concentration of Al (Al=0, 2, 3, 6, and 12 at.%) were deposited using dc magnetron sputter
ing by varying the nitrogen partial pressure between 0 to 100%. The structural and magnetic properties of the films were studied using X-ray diffraction and polarized neutron reflectivity. It was observed that at the lowest doping level (2 at.% of Al), nitrogen rich non-magnetic Fe-N phase gets formed at a lower nitrogen partial pressure as compared to the un-doped sample. Interestingly, we observed that as Al doping is increased beyond 3at.%, nitrogen rich non-magnetic Fe-N phase appears at higher nitrogen partial pressure as compared to un-doped sample. The thermal stability of films were also investigated. Un-doped Fe-N films deposited at 10% nitrogen partial pressure possess poor thermal stability. Doping of Al at 2at.% improves it marginally, whereas, for 3, 6 and 12at.% Al doping, it shows significant improvement. The obtained results have been explained in terms of thermodynamics of Fe-N and Al-N.