We report a structural transition found in Ca10(Ir4As8)(Fe2-xIrxAs2)5, which exhibits superconductivity at 16 K. The c-axis parameter is doubled below a structural transition temperature of approximately 100 K, while the tetragonal symmetry with spac
e group P4/n (No.85) is unchanged at all temperatures measured. Our synchrotron x-ray diffraction study clearly shows iridium ions at a non-coplanar position shift along the z-direction at the structural phase transition. We discuss that the iridium displacements affect superconductivity in Fe2As2 layers.
We report a structural transition found in Ca10(Ir4As8)(Fe2-xIrxAs2)5, which exhibits superconductivity at 16 K, with a layer of divalent iridium coordinated by arsenic in between Fe2As2 layers. The c-axis parameter is doubled below a structural tran
sition temperature of approximately 100 K, while the tetragonal symmetry with space group P4/n (No.85) is unchanged at all temperatures measured. Our synchrotron x-ray diffraction study clearly shows displacements along the z-direction occur in half of the iridium sites, resulting in a complex orbital ordering pattern. Combining our theoretical calculation of the 5d orbital energies with structural data, we propose the iridium orbital crossover transition between the dxy and dz2 orbitals.
We report results of 75As nuclear magnetic resonance (NMR) experiments on a self-flux grown high-quality single crystal of SrFe2As2. The NMR spectra clearly show sharp first-order antiferromagnetic (AF) and structural transitions occurring simultaneo
usly. The behavior in the vicinity of the transition is compared with our previous study on BaFe2As2. No significant difference was observed in the temperature dependence of the static quantities such as the AF splitting and electric quadrupole splitting. However, the results of the NMR relaxation rate revealed difference in the dynamical spin fluctuations. The stripe-type AF fluctuations in the paramagnetic state appear to be more anisotropic in BaFe2As2 than in SrFe2As2.
We report results of 75As nuclear magnetic resonance (NMR) experiments on a self-flux grown single crystal of BaFe2As2. A first-order antiferromagnetic (AF) transition near 135 K was detected by the splitting of NMR lines, which is accompanied by sim
ultaneous structural transition as evidenced by a sudden large change of the electric field gradient tensor at the As site. The NMR results lead almost uniquely to the stripe spin structure in the AF phase. The data of spin-lattice relaxation rate indicate development of anisotropic spin fluctuations of the stripe-type with decreasing temperature in the paramagnetic phase.