We have performed low-temperature specific heat $C$ and thermal conductivity $kappa$ measurements on the Ni-pnictide superconductors BaNi$_2$As$_2$ ($T_mathrm{c}$=0.7 K and SrNi$_2$P$_2$ ($T_mathrm{c}$=1.4 K). The temperature dependences $C(T)$ and $
kappa(T)$ of the two compounds are similar to the results of a number of s-wave superconductors. Furthermore, the concave field responses of the residual $kappa$ for BaNi$_2$As$_2$ rules out the presence of nodes on the Fermi surfaces. We postulate that fully gapped superconductivity could be universal for Ni-pnictide superconductors. Specific heat data on Ba$_{0.6}$La$_{0.4}$Ni$_2$As$_2$ shows a mild suppression of $T_mathrm{c}$ and $H_mathrm{c2}$ relative to BaNi$_2$As$_2$.
We report the results of the angular-dependent magnetoresistance oscillations (AMROs), which can determine the shape of bulk Fermi surfaces in quasi-two-dimensional (Q2D) systems, in a highly hole-doped Fe-based superconductor KFe$_2$As$_2$ with $T_c
approx$ 3.7 K. From the AMROs, we determined the two Q2D FSs with rounded-square cross sections, corresponding to 12% and 17% of the first Brillouin zone. The rounded-squared shape of the FS cross section is also confirmed by the analyses of the interlayer transport under in-plane fields. From the obtained FS shape, we infer the character of the 3d orbitals that contribute to the FSs.
High-pressure electrical resistivity measurements up to 3.0GPa have been performed on EuFe2As2 single crystals with residual resistivity ratios RRR=7 and 15. At ambient pressure, a magnetic / structural transition related to FeAs-layers is observed a
t T0 =190K and 194K for samples with RRR=7 and 15, respectively. Application of hydrostatic pressure suppresses T0, and then induces similar superconducting behavior in the samples with different RRR values. However, the critical pressure 2.7GPa, where T0=0, for the samples with RRR=15 is slightly but distinctly larger than 2.5GPa for the samples with RRR=7.
We report the synthesis and physical properties of single crystals of stoichiometric BaNi2As2 that crystalizes in the ThCr2Si2 structure with lattice parameters a = 4.112(4) AA and c = 11.54(2) AA. Resistivity and heat capacity show a first order pha
se transition at T_0 = 130 K with a thermal hysteresis of 7 K. The Hall coefficient is weakly temperature dependent from room temperature to 2 K where it has a value of -4x10^{-10} Omega-cm/Oe. Resistivity, ac-susceptibility, and heat capacity find evidence for bulk superconductivity at T_c = 0.7 K. The Sommerfeld coefficient at T_c is 11.6 pm 0.9 mJ/molK^2. The upper critical field is anisotropic with initial slopes of dH_{c2}^{c}/dT = -0.19 T/K and dH_{c2}^{ab}/dT = -0.40 T/K, as determined by resistivity.