We report structural evidence of dynamic reorganization in vortex matter in clean NbSe$_2$ by joint small angle neutron scattering and ac-susceptibility measurements. The application of oscillatory forces in a transitional region near the order-disor
der transition results in robust bulk vortex lattice configurations with an intermediate degree of disorder. These dynamically-originated configurations correlate with intermediate pinning responses previously observed, resolving a long standing debate regarding the origin of such responses.
We present small-angle neutron scattering (SANS) and Bitter decoration studies of the superconducting vortices in Ba(Fe$_{0.93}$Co$_{0.07}$)$_2$As$_2$}. A highly disordered vortex configuration is observed at all measured fields, and is attributed to
strong pinning. This conclusion is supported by the absence of a Meissner rim in decoration images obtained close to the sample edge. The field dependence of the magnitude of the SANS scattering vector indicates vortex lattice domains of (distorted) hexagonal symmetry, consistent with the decoration images which show primarily 6-fold coordinated vortex domains. An analysis of the scattered intensity shows that this decreases much more rapidly than expected from estimates of the upper critical field, consistent with the large degree of disorder.
The magnetic field distribution around the vortices in TmNi2B2C in the paramagnetic phase was studied experimentally as well as theoretically. The vortex form factor, measured by small-angle neutron scattering, is found to be field independent up to
0.6 Hc2 followed by a sharp decrease at higher fields. The data are fitted well by solutions to the Eilenberger equations when paramagnetic effects due to the exchange interaction with the localized 4f Tm moments are included. The induced paramagnetic moments around the vortex cores act to maintain the field contrast probed by the form factor.