We present the first study of codoped iron-arsenide superconductors of the 122 family (Sr/Ba)_(1-x)K_xFe_(2-y)Co_yAs_2 with the purpose to increase the upper critical field H_c2 compared to single doped (Sr/Ba)Fe_2As_2 materials. H_c2 was investigate
d by measuring the magnetoresistance in high pulsed magnetic fields up to 64 T. We find, that H_c2 extrapolated to T = 0 is indeed enhanced significantly to ~ 90 T for polycrystalline samples of Ba_0.55K_0.45Fe_1.95Co_0.05As_2 compared to ~75 T for Ba_0.55K_0.45Fe_2As_2 and BaFe_1.8Co_0.2As_2 single crystals. Codoping thus is a promising way for the systematic optimization of iron-arsenic based superconductors for magnetic-field and high-current applications.
Low-temperature (T) heat-capacity measurements under hydrostatic pressure of up to p=2.1 GPa have been performed on single-crystalline CeCu2Si2. A broad superconducting (SC) region exists in the T-p phase diagram. In the low-pressure region antiferro
magnetic spin fluctuations and in the high-pressure region valence fluctuations had previously been proposed to mediate Cooper pairing. We could identify these two distinct SC regions. We found different thermodynamic properties of the SC phase in both regions, supporting the proposal that different mechanisms might be implied in the formation of superconductivity.
We studied the temperature-pressure phase diagram of EuFe2As2 by measurements of the electrical resistivity. The antiferromagnetic spin-density-wave transition at T_0 associated with the FeAs-layers is continuously suppressed with increasing pressure
, while the antiferromagnetic ordering temperature of the Eu 2+ moments seems to be nearly pressure independent up to 2.6 GPa. Above 2 GPa a sharp drop of the resistivity, rho(T), indicates the onset of superconductivity at T_c approx 29.5 K. Surprisingly, on further reducing the temperature rho(T) is increasing again and exhibiting a maximum caused by the ordering of the Eu 2+ moments, a behavior which is reminiscent of re-entrant superconductivity as it is observed in the ternary Chevrel phases or in the rare-earth nickel borocarbides.
The heavy-fermion superconductor CeCoIn5 is the first material, where different experimental probes show strong evidence pointing to the realization of the Fulde-Ferrell-Larkin-Ovchinnikov (FFLO) state. The inhomogeneous superconducting FFLO state wi
th a periodically modulated order parameter was predicted to appear in Pauli-limited, sufficiently clean type-II superconductors already more than 40 years ago. On the other hand, CeCoIn5 is supposed to be close to a magnetic quantum critical point (QCP) showing strong antiferromagnetic (AFM) spin fluctuations (SF) at atmospheric pressure. We studied the evolution of the FFLO phase away from the influence of the strong AFM-SF by heat capacity experiments under pressure (0 GPa <= P <= 1.5 GPa, 0 T <= mu_0 H <= 14 T, and 100 mK <= T <= 4 K). Our results prove the stability of the the FFLO phase under pressure. It even expands, while the Pauli-limiting becomes weaker and the AFM-SF are suppressed. This shows the intriguing influence of the AFM-SF on the FFLO state.