We report ac susceptibility measurements of polycrystalline CePt_3Si down to 60 mK and in applied fields up to 9 T. In zero field, a full Meissner state emerges at temperatures T/Tc < 0.3, where Tc=0.65 K is the onset transition temperature. Though t
ransport measurements show a relatively high upper critical field Bc2 ~ 4-5 T, the low temperature susceptibility, chi, is quite fragile to applied field, with chi diminishing rapidly in fields of a few kG. Interestingly, the field dependence of chi is well described by the power law, 4pichi=(B/B_c)^{1/2}, where Bc is the field at which the onset of resistance is observed in transport measurements.
We report the magnetotransport properties of thin polycrystalline films of the recently discovered non-oxide perovskite superconductor MgCNi3. CNi3 precursor films were deposited onto sapphire substrates and subsequently exposed to Mg vapor at 700 C.
We report transition temperatures (Tc) and critical field values (Hc2) of MgCNi3 films ranging in thickness from 7.5 nm to 100 nm. Films thicker than ~40 nm have a Tc ~ 8 K, and an upper critical field Hc2 ~ 14 T, which are both comparable to that of polycrystalline powders. Hall measurements in the normal state give a carrier density, n =-4.2 x 10^22 cm^-3, that is approximately 4 times that reported for bulk samples.