We show that the morphology of the initial monolayers of InP on Al0.48In0.52As grown by metalorganic vapor-phase epitaxy does not follow the expected layer-by-layer growth mode of lattice-matched systems, but instead develops a number of low-dimensio
nal structures, e.g., quantum dots and wires. We discuss how the macroscopically strain-free heteroepitaxy might be strongly affected by local phase separation/alloying-induced strain and that the preferred aggregation of adatom species on the substrate surface and reduced wettability of InP on AlInAs surfaces might be the cause of the unusual (step) organization and morphology
We present a systematic study of the morphology of homoepitaxial InP films grown by metalorganic vapor-phase epitaxy which are imaged with ex situ atomic force microscopy. These films show a dramatic range of different surface morphologies as a funct
ion of the growth conditions and substrate (growth temperature, V/III ratio, and miscut angle < 0.6deg and orientation toward A or B sites), ranging from stable step flow to previously unreported strong step bunching, over 10 nm in height. These observations suggest a window of growth parameters for optimal quality epitaxial layers. We also present a theoretical model for these growth modes that takes account of deposition, diffusion, and dissociation of molecular precursors, and the diffusion and step incorporation of atoms released by the precursors. The experimental conditions for step flow and step bunching are reproduced by this model, with the step bunching instability caused by the difference in molecular dissociation from above and below step edges, as was discussed previously for GaAs (001).
A virtual substrate for high quality InAs epitaxial layer has been attained via metalorganic vapor-phase epitaxy growth of Sb-assisted InxGa1-xAs metamorphic buffers, following a convex compositional continuous gradient of the In content from x = 53
% to 100 %. The use of trimethylantimony (or its decomposition products) as a surfactant has been found to crucially enable the control over the defect formation during the relaxation process. Moreover, an investigation of the wafer offcut-dependence of the defect formation and surface morphology has enabled the achievement of a reliably uniform growth on crystals with offcut towards the [111]B direction.