We present an extensive irradiation study involving five state-of-the-art Nb3Sn wires which were subjected to sequential neutron irradiation up to a fast neutron fluence of 1.6 * 10^22 m^-2 (E > 0.1 MeV). The volume pinning force of short wire sample
s was assessed in the temperature range from 4.2 to 15 K in applied fields of up to 7 T by means of SQUID magnetometry in the unirradiated state and after each irradiation step. Pinning force scaling computations revealed that the exponents in the pinning force function differ significantly from those expected for pure grain boundary pinning, and that fast neutron irradiation causes a substantial change in the functional dependence of the volume pinning force. A model is presented, which describes the pinning force function of irradiated wires using a two-component ansatz involving a point-pinning contribution stemming from radiation induced pinning centers. The dependence of this point-pinning contribution on fast neutron fluence appears to be a universal function for all examined wire types.
We report on measurements of the superconducting properties of FeSe05Te05 thin films grown on lanthanum aluminate. The films have high transition temperatures (above 19 K) and sharp resistive transitions in fields up to 15 T. The temperature dependen
ce of the upper critical field and the irreversibility lines are steep and anisotropic, as recently reported for single crystals. The critical current densities, assessed by magnetization measurements in a vector VSM, were found to be well above 10^9 Am-2 at low temperatures. In all samples, the critical current as a function of field orientation has a maximum, when the field is oriented parallel to the film surface. The maximum indicates the presence of correlated pinning centers. A minimum occurs in three films, when the field is applied perpendicular to the film plane. In the forth film, instead, a local maximum caused by c-axis correlated pinning centers was found at this orientation. The irradiation of two films with fast neutrons did not change the properties drastically, where a maximum enhancement of the critical current by a factor of two was found.
Investigating the role of disorder in superconductors is an essential part of characterizing the fundamental superconducting properties as well as assessing potential applications of the material. In most cases, the information available on the defec
t matrix is poor, making such studies difficult, but the situation can be improved by introducing defects in a controlled way, as provided by neutron irradiation. In this work, we analyze the effects of neutron irradiation on a Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ single crystal. We mainly concentrate on the magnetic properties which were determined by magnetometry. Introducing disorder by neutron irradiation leads to significant effects on both the reversible and the irreversible magnetic properties, such as the transition temperature, the upper critical field, the anisotropy, and the critical current density. The results are discussed in detail by comparing them with the properties in the unirradiated state.