The evolution of magnetism and superconductivity in Ce$_2$Rh$_{1-x}$Pd$_x$In$_8$ solid solutions has been studied within the entire concentration range by means of thermodynamic and magnetic measurements at ambient pressure and at temperatures betwee
n 0.35 K and room temperature. For this purpose, single crystals with Pd concentrations x = 0, 0.10, 0.15, 0.30, 0.45, 0.55, 0.85 and 1 have been grown from In self-flux and characterized by x-ray diffraction and microprobe analysis. Starting from the antiferromagnet Ce$_2$RhIn$_8$, the Neel temperature gradually decreases with increasing Pd concentration and the antiferromagnetism has disappeared for $x ge 0.45$. Superconductivity has been observed only for Ce$_2$PdIn$_8$.
Solution growth of single crystals of the recently reported new compound Ce2PdIn8 was investigated. When growing from a stoichiometry in a range 2:1:20 - 2:1:35, single crystals of CeIn3 covered by a thin (~50 um) single-crystalline layer of Ce2PdIn8
were mostly obtained. Using palladium richer compositions the thickness of the Ce2PdIn8 layers were increased, which allowed mechanical extraction of single-phase slabs of the desired compound suitable for a thorough study of magnetism and superconductivity. In some solution growth products also CePd3In6 (LaNi3In6 - type of structure) and traces of phases with the stoichiometry CePd2In7, Ce1.5Pd1.5In7 (determined only by EDX) have been identified. Magnetic measurements of the Ce2PdIn8 single crystals reveal paramagnetic behaviour of the Ce3+ ions with significant magnetocrystalline anisotropy. Above 70 K the magnetic susceptibility follows the Curie-Weiss law with considerably different values of the paramagnetic Curie temperature, for the magnetic field applied along the a- (-90 K) and c-(-50 K) axis. Below the reported critical temperature for superconductivity Tc (0.69 K) the electrical resistivity drops to zero. Comparative measurements of the electrical resistivity, heat capacity and AC susceptibility of several crystals reveal that the superconducting transition is strongly sample-dependent.