The valence state of Ce in a canonical heavy fermion compound CeRu2Si2 has been investigated by synchrotron X-ray absorption spectroscopy at 1.8 K in high magnetic fields of up to 40 T. The valence was slightly larger than for the pure trivalent stat
e (Ce3+: f1), as expected in heavy fermion compounds, and it decreased toward the trivalent state as the magnetic field was increased. The field-induced valence reduction indicates that the itinerant character of the 4f electrons in CeRu2Si2 was suppressed by a strong magnetic field. The suppression was gradual and showed characteristic magnetic field dependence, which reflects the metamagnetism around Hm sim 8 T. The itinerant character persisted, even at 40 T (sim 5Hm), suggesting that the Kondo bound state is continuously broken by magnetic fields and that it should completely collapse at fields exceeding 200 T.
We report the magnetic field dependent dc magnetization and the pressure-dependent (pmax ~ 16 kbar) ac susceptibilities Xp(T) on both powder and bulk multiferroic BiMnO3 samples, synthesized in different batches under high pressure. A clear ferromagn
etic (FM) transition is observed at TC ~ 100 K, and increases with magnetic field. The magnetic hysteresis behavior is similar to that of a soft ferromagnet. Ac susceptibility data indicate that both the FM peak and its temperature (TC) decrease simultaneously with increasing pressure. Interestingly, above a certain pressure (9 ~ 11 kbar), another peak appears at Tp ~ 93 K, which also decreases with increasing pressure, with both these peaks persisting over some intermediate pressure range (9 ~ 13 kbar). The FM peak disappears with further application of pressure; however, the second peak survives until present pressure limit (pmax ~ 16 kbar). These features are considered to originate from the complex interplay of the magnetic and orbital structure of BiMnO3 being affected by pressure.