A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a readily scal
able, industrial technique, to 91% of their maximum theoretical density. The macroscopic critical current density derived from the trapped field data using the Biot-Savart law is consistent with the measured local critical current density. From this we conclude that critical current density, and therefore trapped field performance, is limited by the flux pinning available in MgB2, rather than by lack of connectivity. This suggests strongly that both increasing sample size and enhancing pinning through doping will allow further increases in trapped field performance of bulk MgB2.
The Fe-based superconductors (FBS) are an important new class of superconducting materials. As with any new superconductor with a high transition temperature and upper critical field, there is a need to establish what their applications potential mig
ht be. Applications require high critical current densities, so the usefulness of any new superconductor is determined both by the capability to develop strong vortex pinning and by the absence or ability to overcome any strong current-limiting mechanisms of which grain boundaries in the cuprates are a cautionary example. In this review we first consider the positive role that grain boundary properties play in the metallic, low temperature superconductors and then review the theoretical background and current experimental data relating to the properties of grain boundaries in FBS polycrystals, bi-crystal thin films, and wires. Based on this evidence, we conclude that grain boundaries in FBS are weak linked in a qualitatively similar way to grain boundaries in the cuprate superconductors, but also that the effects are a little less marked. Initial experiments with the textured substrates used for cuprate coated conductors show similar benefit for the critical current density of FBS thin films too. We also note that the particular richness of the pairing symmetry and the multiband parent state in FBS may provide opportunities for grain boundary modification as a better understanding of their pairing state and grain boundary properties are developed.
We discuss predictions of five proposed theories for the critical state of type-II superconductors accounting for both flux cutting and flux transport (depinning). The theories predict different behaviours for the ratio $E_y/E_z$ of the transverse an
d parallel components of the in-plane electric field produced just above the critical current of a type-II superconducting slab as a function of the angle of an in-plane applied magnetic field. We present experimental results measured using an epitaxially grown YBCO thin film favoring one of the five theories: the extended elliptic critical-state model. We conclude that when the current density $bm J$ is neither parallel nor perpendicular to the local magnetic flux density $bm B$, both flux cutting and flux transport occur simultaneously when $J$ exceeds the critical current density $J_c$, indicating an intimate relationship between flux cutting and depinning. We also conclude that the dynamical properties of the superconductor when $J$ exceeds $J_c$ depend in detail upon two nonlinear effective resistivities for flux cutting ($rho_c$) and flux flow ($rho_f$) and their ratio $r= rho_c/rho_f$.
We identify a scalable, practical route to fabricating a superconducting diode. The device relies for its function on the barrier to flux vortex entry being reduced at the substrate interface of a superconducting pinning enhanced YBa2Cu3O7-d nano-com
posite film. We show that these composite systems provide a practical route to fabricating a useful superconducting diode and demonstrate the rectification of an alternating current.
We report on the in-plane magnetic field (H) dependence of the critical current density (Jc) in meandered and planar single grain boundaries (GBs) isolated in YBa2Cu3O7-d (YBCO) coated conductors. The Jc(H)properties of the planar GB are consistent w
ith those previously seen in single GBs of YBCO films grown on SrTiO3 bi-crystals. In the straight boundary a characteristic flux channeling regime when H is oriented near the GB plane, associated with a reduced Jc, is seen. The meandered GB does not show vortex channeling since it is not possible for a sufficient length of vortex line to lie within it.
The critical currents of MOD/RABiTS and PLD/IBAD coated conductors have been measured as a function of magnetic field orientation and compared to films grown on single crystal substrates. By varying the orientation of magnetic field applied in the pl
ane of the film, we are able to determine the extent to which current flow in each type of conductor is percolative. Standard MOD/RABiTS conductors have also been compared to samples whose grain boundaries have been doped by diffusing Ca from an overlayer. We find that undoped MOD/RABiTS tapes have a less anisotropic in-plane field dependence than PLD/IBAD tapes and that the uniformity of critical current as a function of in-plane field angle is greater for MOD/RABiTS samples doped with Ca.
Most measurements of critical current densities in YBa$_2$Cu$_3$O$_{7-delta}$ thin films to date have been performed on films where the textit{c}-axis is grown normal to the film surface. With such films, the analysis of the dependence of $j_c$ on th
e magnetic field angle is complex. The effects of extrinsic contributions to the angular field dependence of $j_c$, such as the measurement geometry and disposition of pinning centres, are convoluted with those intrinsically due to the anisotropy of the material. As a consequence of this, it is difficult to distinguish between proposed FLL structure models on the basis of angular critical current density measurements on textit{c}-axis films. Films grown on mis-cut (vicinal) substrates have a reduced measurement symmetry and thus provide a greater insight into the critical current anisotropy. In this paper previous descriptions of the magnetic field angle dependence of $j_c$ in YBa$_2$Cu$_3$O$_{7-delta}$ are reviewed. Measurements on YBa$_2$Cu$_3$O$_{7-delta}$ thin films grown on a range of vicinal substrates are presented and the results interpreted in terms of the structure and dimensionality of the FLL in YBa$_2$Cu$_3$O$_{7-delta}$. There is strong evidence for a transition in the structure of the flux line lattice depending on magnetic field magnitude, orientation and temperature. As a consequence, a simple scaling law can not, by itself, describe the observed critical current anisotropy in YBa$_2$Cu$_3$O$_{7-delta}$. The experimentally obtained $j_c(theta)$ behaviour of YBCO is successfully described in terms of a kinked vortex structure for fields applied near parallel to the textit{a-b} planes.