We investigated the microwave properties of polymer based metacomposites containing hybridized parallel Fe- and Co-based microwire arrays. A dual-band left-handed feature was observed in the frequency bands of 1.5 to 5.5 GHz and 9 to 17 GHz, indicate
d by two transmission windows associated with ferromagnetic resonance of Fe-based microwires and long range dipolar resonance between the wire arrays. The plasma frequency after hybridization is significantly increased due to the enhanced effective diameter through the wire-wire interactions between the Fe- and Co- microwire couples. These results offer essential perspectives in designing the multi-band metamaterial for microwave applications such as sensors and cloaking devices.
The microwave properties of glass-fibers reinforced polymer composite embedded with an orthogonal array of Fe77Si10B10C3 microwires have been investigated. The composites containing orthogonal wire arrays display a remarkable transmission window in t
he frequency band of 1 to 6 GHz under zero external magnetic field indicating an intrinsic double-negative-index characteristic. The polymer matrices have proved to exert a synergistic effect on the microwave properties, which is responsible for the disappearance of the transmission windows when Ek is perpendicular to the glass fiber direction. The plasma frequency of the orthogonal microwire array composite is higher than that of the parallel microwire array with identical wire spacing; this could be attributed to the enhanced microwire-wave interaction induced by the axial electrical components on the additional layer of perpendicular wires. All these features make this new kind of orthogonal microwire composites promising for potential cloaking and sensing applications.