We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2 (BFAP) single crystals by small-angle neutron scattering (SANS). With the field along the c-axis, a nearly isotropic hexagonal VL was formed in the field range from 1 to 16
T, which is a record for this technique in the pnictides, and no symmetry changes in the VL were observed. The temperature-dependence of the VL signal was measured and confirms the presence of (non d-wave) nodes in the superconducting gap structure for measurements at 5 T and below. The nodal effects were suppressed at high fields. At low fields, a VL reorientation transition was observed between 1 T and 3 T, with the VL orientation changing by 45{deg}. Below 1 T, the VL structure was strongly affected by pinning and the diffraction pattern had a fourfold symmetry. We suggest that this (and possibly also the VL reorientation) is due to pinning to defects aligned with the crystal structure, rather than being intrinsic.
Understanding the mechanism and symmetry of electron pairing in iron-based superconductors represents an important challenge in condensed matter physics [1-3]. The observation of magnetic flux lines - vortices - in a superconductor can contribute to
this issue, because the spatial variation of magnetic field reflects the pairing. Unlike many other iron pnictides, our KFe2As2 crystals have very weak vortex pinning, allowing small-angle-neutron-scattering (SANS) observations of the intrinsic vortex lattice (VL). We observe nearly isotropic hexagonal packing of vortices, without VL-symmetry transitions up to high fields along the fourfold c-axis of the crystals, indicating rather small anisotropy of the superconducting properties around this axis. This rules out gap nodes parallel to the c-axis, and thus d-wave and also anisotropic s-wave pairing [2, 3]. The strong temperature-dependence of the intensity down to T<<Tc indicates either widely different full gaps on different Fermi surface sheets, or nodal lines perpendicular to the axis.