Enhanced thermoelectric performance in spark plasma textured bulk n-type BiTe2.7Se0.3 and p-type Bi0.5Sb1.5Te3

Bulk p and n-type bismuth telluride were prepared using spark plasma texturization method. The texture development along the uniaxial load in the 001 direction is confirmed from both x-ray diffraction analysis and Electron Backscattering Diffraction measurements. Interestingly, those textured samples outperform the samples prepared by conventional spark plasma sintering (SPS) leading to a reduced thermal conductivity in the ab-plane. The textured samples of n- type BiTe2.7Se0.3 and p-type Bi0.5Sb1.5Te3 showed a 42% and 33% enhancement in figure of merit at room temperature respectively, as compared to their SPS counterparts, opening the route for applications.

Growth and texture of Spark Plasma Sintered Al2O3 ceramics: a combined analysis of X-rays and Electron Back Scatter Diffraction

Textured alumina ceramics were obtained by Spark Plasma Sintering (SPS) of undoped commercial a-Al2O3 powders. Various parameters (density, grain growth, grain size distribution) of the alumina ceramics, sintered at two typical temperatures 1400{deg}C and 1700{deg}C, are investigated. Quantitative textural and structural analysis, carried out using a combination of Electron Back Scattering Diffraction (EBSD) and X-ray diffraction (XRD), are represented in the form of mapping, and pole figures. The mechanical properties of these textured alumina ceramics include high elastic modulus and hardness value with high anisotropic nature, opening the door for a large range of applications